A Hierarchical and Multiphase Nanolaminated Alloy with an Excellent Combination of Tensile Properties

Yindong Shi,Ming Li,Defeng Guo,Guosheng Zhang,Qian Zhang,Xiaohong Li,Xiangyi Zhang

DOI: https://doi.org/10.1016/j.msea.2014.07.081

2014-01-01

Abstract:Ti alloys that possess a fine fully lamellar structure generally exhibit high strength but limited ductility. In this study, a hierarchical and multiphase nanolaminated structure that consists of large microscale primary alpha(p) grains (similar to 1.5 m), sub-microscale a plates (similar to 200 nm) and nanoscale acicular isothermal (orthorhombic) alpha'' martensites (similar to 15 nm) is produced in a TiZrAlV alloy with a fine (similar to 12 mu m) beta grain size through the use of severe plastic deformation (SPD) combined with subsequent recrystallisation annealing and aging treatments. This specific structure results in an excellent combination of tensile properties, e.g., an ultimate tensile strength of sigma(b)similar to 1545 MPa and an elongation to failure of epsilon(f)similar to 7.9. The present study demonstrates an alternative route for enhancing the mechanical properties of titanium alloys with laminated structures. (C) 2014 Elsevier B.V. All rights reserved.