Abstract:The upcycling of waste materials to fabricate high-performance electrode materials is of great interest for future energy storage devices. In this paper, we suggest an efficient strategy of upcycling waste cotton fabrics (WCFs) into freestanding carbon fabrics (CFs) via two-step thermal treatment. The prepared CFs exhibited a large specific surface area, multimodal pore structures, flexible free-standing structural properties, and good electrical conductivity. The electrochemical performance of the CFs was investigated by cyclic voltammetry, galvanostatic charging/discharging tests, and electrochemical impedance spectroscopy. In a three-electrode system, the binder-free CF-based electrode exhibited a gravimetric specific capacitance of 198 F g−1 at 1 A g−1 in a 6 M KOH aqueous electrolyte. The binder-free and current collector-free CF-based symmetric capacitor showed an areal capacitance of 262 mF cm−2 at 2 mA cm−2, a gravimetric capacitance of 29.4 F g−1 at 1 A g−1, a maximum gravimetric power density of ∼3000 W kg−1 at an energy density of 3.21 Wh kg−1, an areal power density of ∼25,000 mW cm−2 at an energy density of 23.53 mWh cm−2, and an excellent cycle stability of ∼100 % at 100 mA cm−2 after 10,000 cycles. These results reveal that WCFs can be a promising precursor material for the preparation of free-standing carbon-based electrode materials in various energy storage devices.

Structure and Electrochemical Performance of Hollow Tube Activated Carbon Prepared from Cotton As Electrode Material for Electric Double Layer Capacitor

Control of Nano Grains and Wide Carbocyclic Layer Space of Forming Active Carbon with Extraordinary Capacitance Characteristics in Supercapacitors

Preparation and Electrochemical Performance of Hollow Activated Carbon Fiber Self-Supported Electrode for Supercapacitor

Mesoporous Carbon Materials As Electrodes for Electrochemical Double-Layer Capacitor

Cotton fabrics-derived flexible nitrogen-doped activated carbon cloth for high-performance supercapacitors in organic electrolyte

Flute Type Micropores Activated Carbon from Cotton Stalk for High Performance Supercapacitors

Free-standing carbon network with enhanced capacitive performance synthesized via green H 2 O 2 activation

Porous Cotton-derived Carbon: Synthesis, Microstructure and Supercapacitive Performance

Biobased Nano Porous Active Carbon Fibers for High-Performance Supercapacitors

Honeycomb-like Hierarchical Porous Activated Carbons from Biomass Waste with Ultrahigh Specific Surface Area for High-Rate Electrochemical Capacitors

Oxygen-rich Hierarchical Porous Carbon Derived from Coal Tar Pitch for Superior Electric Double Layer Capacitor Application

Porous carbon with tailored pore size for electric double layer capacitors application

Preparation and Characterization of Free-Standing Electrode Materials from Waste Cotton Fabrics for Electric Double-Layer Capacitors

Preparation of Nitrogen-containing Activated Carbon from Waste Medium Density Fiberboard for Electric Double Layer Capacitor

The Effect of the Ratio of KOH to Carbon on the Pore Structure and the Capacitance Characteristic of Activated Carbon

Tailoring Macro/Meso/Microporous Structures of Cellophane Noodle-Derived Activated Carbon for Electric Double-Layer Capacitors

Porous carbon made from rice husk as electrode material for electrochemical double layer capacitor

Electrochemical Characterization of Mesopore Activated Carbon Electrodes for Electric Double-Layer Capacitors

Corncob-Derived Activated Carbon as Electrode Material for High-Performance Supercapacitor

Facile Synthesis of Nitrogen-Containing Porous Carbon As Electrode Materials for Superior-Performance Electrical Double-Layer Capacitors

Versatile Activated Carbon Fibers Derived from the Cotton Fibers Used as CO2 Solid-State Adsorbents and Electrode Materials