Abstract:The fabrication of dual-doped activated carbon with a hierarchical pore structure is an effective way for the preparation of the high performance carbon-based electric double layer capacitor. Herein, nitrogen and sulfur dual-doped activated carbon (NSC) with hierarchical pore structure was obtained by directly carbonizing/activating polymer-based blend monolith. The as-obtained NSC samples exhibit a high specific surface area (1570-2550 cm2 g−1), a developed hierarchically pore structure, and have an appropriate nitrogen and sulfur content. Furthermore, originating from the synergistic effect by pore structure, heteroatom, and proper graphitized crystal structure, the optimized NSC-based electrode exhibits a high specific capacitance of 330.5 F g−1 at a current density of 0.5 A g−1, superior rate capability of 66% at 20 A g−1 and acceptable cycling stability in the three-electrode system. Meanwhile, the assembled carbon-based symmetric capacitor exhibits an acceptable energy density and a remarkable power density of 11 kW kg−1 with 6 mol L−1 KOH as the aqueous electrolyte. These results demonstrate that the as-resulting NSC could be a competitive candidate for carbon-based electrode materials, and this work would be a valuable exploration that as a facile synthetic strategy to prepared dual-doped activated carbon for electric double layer capacitor.

Tailoring Macro/Meso/Microporous Structures of Cellophane Noodle-Derived Activated Carbon for Electric Double-Layer Capacitors

Dual-doping activated carbon with hierarchical pore structure derived from polymeric porous monolith for high performance EDLC

Control of Nano Grains and Wide Carbocyclic Layer Space of Forming Active Carbon with Extraordinary Capacitance Characteristics in Supercapacitors

Honeycomb-like Hierarchical Porous Activated Carbons from Biomass Waste with Ultrahigh Specific Surface Area for High-Rate Electrochemical Capacitors

Nanostructured activated carbons from natural precursors for electrical double layer capacitors

Activated Carbon Nanochains With Tailored Micro-Meso Pore Structures And Their Application For Supercapacitors

Electrochemical Characterization of Mesopore Activated Carbon Electrodes for Electric Double-Layer Capacitors

Bamboo-Based Mesoporous Activated Carbon for High-Power-Density Electric Double-Layer Capacitors

KOH Activation of Needle Coke to Develop Activated Carbons for High-Performance EDLC

Synthesis of activated carbon nanospheres with hierarchical porous structure for high volumetric performance supercapacitors

Synthesis of a Very High Specific Surface Area Active Carbon and Its Electrical Double-Layer Capacitor Properties in Organic Electrolytes

Preparation of Mesophase-Pitch-based Activated Carbons for Electric Double Layer Capacitors with High Energy Density

Influence of Pore Structure of Coal-based Activated Carbons on Electric Double Layer Capacitance

Microporous and Grain-Sized Design of High-Yield Porous Carbon Materials by Using Potassium Acetate and p -Phenylenediamine

The Effect of Pre-Carbonization of Mesophase Pitch-Based Activated Carbons on Their Electrochemical Performance for Electric Double-Layer Capacitors

Porous carbon with tailored pore size for electric double layer capacitors application

Activated carbon with micrometer-scale channels prepared from luffa sponge fibers and their application for supercapacitors

Preparation of kraft lignin-based activated carbon fiber electrodes for electric double layer capacitors using an ionic liquid electrolyte

The Effect of the Ratio of KOH to Carbon on the Pore Structure and the Capacitance Characteristic of Activated Carbon

A quantitative evaluation of the large pore-size effect on the electric double-layer capacitance for high voltage by 19 F-NMR

Ultrafast pore-tailoring of dense microporous carbon for high volumetric performance supercapacitors in organic electrolyte