Abstract:Coal liquefaction pitch is a byproduct rich in polycyclic aromatic hydrocarbon generated during coal liquefaction process, and can be used to prepare porous carbon electrodes for electric double-layer capacitors. However, the effects of the proportion of pore volume in different pore size ranges on the electrochemical properties of porous carbon are still not well investigated. Herein, porous carbon was fabricated from liquefaction pitch and KOH at a mass ratio of 1:2 and activation temperatures of 600–900 °C. The results showed an increase in both specific surface area and total pore volume of the samples with the activation temperature, inconsistent with the changing trend of the specific capacitances due to well-stored electrolyte ions in micropores. In particular, micropores with pore volume diameter below 1 nm greatly impacted the specific capacitance performance of porous carbon. The pore volume with pore width below 1 nm first increased and then decreased with the activation temperature. Among samples, porous carbon prepared at activation temperature of 700 °C delivered the highest specific capacitance of 329 F g−1 at a specific current of 0.5 A g−1, and retained 254 F g−1 of specific capacitance at 20 A g−1 in 6 mol L−1 KOH electrolyte. The reason for this was related to the largest pore volume with pore width below 1 nm (0.43 cm3 g−1). Afterward, the optimized sample was assembled into a symmetrical supercapacitor and test results showed that 96.37% of the initial capacitance was retained after 10,000 cycles at 1 A g−1, suggesting good cycling stability. In sum, the as-prepared porous carbon is very promising for use as electrode material for supercapacitors.

The Effect of Pre-Carbonization of Mesophase Pitch-Based Activated Carbons on Their Electrochemical Performance for Electric Double-Layer Capacitors

Preparation of Mesophase-Pitch-based Activated Carbons for Electric Double Layer Capacitors with High Energy Density

Mesoporous Carbon Materials As Electrodes for Electrochemical Double-Layer Capacitor

Control of Nano Grains and Wide Carbocyclic Layer Space of Forming Active Carbon with Extraordinary Capacitance Characteristics in Supercapacitors

Performance of Electric Double Layer Capacitors Using Active Carbons Prepared from Petroleum Coke by Koh and Vapor Re-Etching

Fabrication and Properties of Double-layer Capacitor with Acetylene Black Electrode

Effect of Porosity and Crystallinity of Activated Carbons for Electrochemical Capacitors

Preparation and Electrochemical Properties of PF-based Activated Carbon

Hierarchical porous carbon derived from carboxylated coal-tar pitch for electrical double-layer capacitors

Porous carbon with tailored pore size for electric double layer capacitors application

Tailoring Macro/Meso/Microporous Structures of Cellophane Noodle-Derived Activated Carbon for Electric Double-Layer Capacitors

Preparation of Nitrogen-containing Activated Carbon from Waste Medium Density Fiberboard for Electric Double Layer Capacitor

Synthesis of a Very High Specific Surface Area Active Carbon and Its Electrical Double-Layer Capacitor Properties in Organic Electrolytes

A quantitative evaluation of the large pore-size effect on the electric double-layer capacitance for high voltage by 19 F-NMR

Activated Carbons and Their Evaluation in Electric Double Layer Capacitors

A novel mesoporous carbon with straight tunnel-like pore structure for high rate electrochemical capacitors

Synthesis of multi-branched porous carbon nanofibers and their application in electrochemical double-layer capacitors

Biobased Nano Porous Active Carbon Fibers for High-Performance Supercapacitors

Liquefaction pitch-based porous carbon: Preparation and relationship between pore structure and electrochemical properties

Controlling and optimizing the morphology and microstructure of 3D interconnected activated carbons for high performance supercapacitors

Preparation and Characterization of Seaweed-based Activated Carbons as Electrode Materials for Electric Double Layer Capacitors