Abstract:Biomasses are promising precursors of porous carbons. However, the complexity in composition and microstructure of biomasses might result in poor quality reproducibility of biomass-derived porous carbons. It is essential to develop reliable approaches to prepare biomass-derived porous carbons. In this work, a nitrogen-doped porous carbon derived from cellulose microfibers of rice straw was prepared. The cellulose microfibers were first extracted from rice straw by alkali treatment. Then, a hydrochar was fabricated by hydrothermal treatment of the cellulose microfibers. Nitrogen-doped porous carbon was finally obtained by calcination under high temperature with K2CO3 and CO(NH2)2 as the activating agent and nitrogen dopant, respectively. The prepared carbon material has an ultrahigh specific surface area (∼2800 m2/g) and a moderate nitrogen doping (1.65 atom %). Consequently, rice-straw-derived porous carbon achieves a remarkable specific capacitance (380.1 F/g at 0.5 A/g) and a good rate capability (61.8% capacitance retention at 50 A/g). In addition, the porous carbon exhibits good cycling stability. The loss of capacitance is only 4.6% after 10 000 charge–discharge cycles. This study provides a robust method for the preparation of porous carbons from lignocellulosic biomasses.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.energyfuels.1c00323?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.energyfuels.1c00323</a>.SEM images of the carbonization product of raw rice straw (Figure S1), SEM images of the carbons prepared with different quantities of K2CO3 (Figure S2), rate capabilities of KRS-x and NKRS-y (Figure S3), CV curves and GCD profiles of RS and KRS (Figures S4 and S5), equivalent electric circuit diagram (Figure S6 and Table S1), comparison in capacitive performance between NKRS and NKRS-N (Figure S7), and comparison of various carbon materials in specific capacitance (Table S2) (<a class="ext-link" href="/doi/suppl/10.1021/acs.energyfuels.1c00323/suppl_file/ef1c00323_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Porous carbon made from rice husk as electrode material for electrochemical double layer capacitor

Green Synthesis of Nitrogen-doped Porous Carbon Derived from Rice Straw for High-performance Supercapacitor Application

Synthesis of rice husk derived porous carbon as low-cost and high-performance electrode material for supercapacitors

Co2SiO4/CoO Heterostructure Anchored on Graphitized Carbon Derived from Rice Husks with Hierarchical Pore As Electrode Material for Supercapacitor

Porous carbon derived from cashew nut husk biomass waste for high-performance supercapacitors

Hydrangea-like N/O codoped porous carbons for high-energy supercapacitors

Rice Hull-Derived Carbon for Supercapacitors: Towards Sustainable Silicon-Carbon Supercapacitors

Hierarchical Micro-/Mesoporous Carbon Derived from Rice Husk by Hydrothermal Pre-Treatment for High Performance Supercapacitor

Control of Nano Grains and Wide Carbocyclic Layer Space of Forming Active Carbon with Extraordinary Capacitance Characteristics in Supercapacitors

Mesoporous Carbon Materials As Electrodes for Electrochemical Double-Layer Capacitor

Facile synthesis of functionalized porous carbon with three-dimensional interconnected pore structure for high volumetric performance supercapacitors

Porous carbon with tailored pore size for electric double layer capacitors application

Conversion of high moisture biomass to hierarchical porous carbon via molten base carbonisation and activation for electrochemical double layer capacitor

One/Two-Step Contribution to Prepare Hierarchical Porous Carbon Derived from Rice Husk for Supercapacitor Electrode Materials

Peanut shell waste derived porous carbon for high-performance supercapacitors

Nitrogen-Doped Porous Carbon Derived from Cellulose Microfibers of Rice Straw for High-Performance Electrodes of Supercapacitors

Preparation of hierarchical porous carbon through one-step KOH activation of coconut shell biomass for high-performance supercapacitor

KHCO3 Chemical-Activated Hydrothermal Porous Carbon Derived from Sugarcane bagasse for Supercapacitor Applications

Hierarchical porous carbon derived from carboxylated coal-tar pitch for electrical double-layer capacitors

Hierarchical Porous Heteroatoms—Co-Doped Activated Carbon Synthesized from Coconut Shell and Its Application for Supercapacitors

Corncob-Derived Activated Carbon as Electrode Material for High-Performance Supercapacitor