Nitrogen-Doped Porous Carbon Derived from Cellulose Microfibers of Rice Straw for High-Performance Electrodes of Supercapacitors

Huachen Liu,Feng Zhang,Zhaofeng Wu,Entian Cui,Lu Yue,Guihua Hou,Luming Wang

DOI: https://doi.org/10.1021/acs.energyfuels.1c00323

2021-05-26

Abstract:Biomasses are promising precursors of porous carbons. However, the complexity in composition and microstructure of biomasses might result in poor quality reproducibility of biomass-derived porous carbons. It is essential to develop reliable approaches to prepare biomass-derived porous carbons. In this work, a nitrogen-doped porous carbon derived from cellulose microfibers of rice straw was prepared. The cellulose microfibers were first extracted from rice straw by alkali treatment. Then, a hydrochar was fabricated by hydrothermal treatment of the cellulose microfibers. Nitrogen-doped porous carbon was finally obtained by calcination under high temperature with K₂CO₃ and CO(NH₂)₂ as the activating agent and nitrogen dopant, respectively. The prepared carbon material has an ultrahigh specific surface area (∼2800 m²/g) and a moderate nitrogen doping (1.65 atom %). Consequently, rice-straw-derived porous carbon achieves a remarkable specific capacitance (380.1 F/g at 0.5 A/g) and a good rate capability (61.8% capacitance retention at 50 A/g). In addition, the porous carbon exhibits good cycling stability. The loss of capacitance is only 4.6% after 10 000 charge–discharge cycles. This study provides a robust method for the preparation of porous carbons from lignocellulosic biomasses.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.energyfuels.1c00323?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.energyfuels.1c00323</a>.SEM images of the carbonization product of raw rice straw (Figure S1), SEM images of the carbons prepared with different quantities of K₂CO₃ (Figure S2), rate capabilities of KRS-<i>x</i> and NKRS-<i>y</i> (Figure S3), CV curves and GCD profiles of RS and KRS (Figures S4 and S5), equivalent electric circuit diagram (Figure S6 and Table S1), comparison in capacitive performance between NKRS and NKRS-N (Figure S7), and comparison of various carbon materials in specific capacitance (Table S2) (<a class="ext-link" href="/doi/suppl/10.1021/acs.energyfuels.1c00323/suppl_file/ef1c00323_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

energy & fuels,engineering, chemical