Abstract:<p>For the hybrid electric vehicle (HEV), accurate prediction of the remaining use life for the power batteries under actual operating conditions is of great significance to the battery power state of charge (SOC) estimation, as well as to the reliability and safety. However, there is little study available to evaluate the battery degradation behavior in real applications. Current battery degradation model is mostly established based on laboratory condition. In such case, charging/discharging scenarios are mostly constant across the battery cycle, and thus, they may be not a good representative of the working condition of the Ni-MH in real application where charging/discharging are frequently altered. Therefore, in this paper, the cycle life degradation characteristics of Ni-MH batteries for HEVs were studied, and an experienced model of cycle life is established based on the data from the real-world driving settings. The cycle life results indicated that the capacity loss is strongly impacted by the charge and discharge rate (C-rate), temperature, and depth of discharge (DOD). A large cycle test matrix is used to collect battery life data to build the model. The test matrix parameters include temperature (25 °C, 45 °C, 55 °C), DOD (0.5, 0.8, 1) and C-rate (1C, 2C, 5C). To verify the reliability of the life model applied to the HEV, the equivalent cycle life test verification of the real vehicle road spectrum was carried out. The test results show that the model can characterize the battery's decay process well.</p>

The Cycling Behavior and Capacity Deterioration Model of Hydride Electrodes in Charging-Discharging Cycling

Capacity Estimation of Lithium-ion Battery Based on Electrochemical Model with Electrolyte Dynamics

The Relation Between the Discharge Capacity and Cycling Number of Mechanically Alloyed MgxNi100−x Amorphous Electrode Alloys

Corrosion Mechanism of Mechanically Alloyed Mg50ni50 and Mg45cu5ni50 Alloys

The relation between discharge capacities anddischarge current densities of hydride electrodes

Development of the cycling life model of Ni-MH power batteries for hybrid electric vehicles based on real-world operating conditions

Electrochemical behaviors of a V3TiNi0.56Hf0.24 alloy electrode during charge–discharge cycling

The Cycling Behaviour of Misch Metal—nickel-Basedmetal Hydride Electrodes and the Effects of Copper Plating on Their Performance

Electrochemical Behaviors Of A V3tini0.5hf0.24 Alloy Electrode During Charge-Discharge Cycling

Degradation model and cycle life prediction for lithium-ion battery used in hybrid energy storage system

Cycling-induced damage of silicon-based lithium-ion batteries: Modeling and experimental validation

Cycling durability and degradation behavior of La–Mg–Ni–Co-type metal hydride electrodes

Changes of some capacities and failure mode of Ni/MH batteries during cycling

A Lithium-Ion Battery Capacity Degradation Correction Method for Off-Design Cycling Conditions

A Study on the Cycling Stability of the Ti–V-based Hydrogen Storage Electrode Alloys

Capacity loss in different charge/discharge cycles of Lithium ion batteries

The Cycle Life and Surface Properties of Ti-based AB2 Metal Hydride Electrodes

Phenomenological modelling of cycling-induced damage in the metal-ion battery electrode

Electro-thermal cycle life model for lithium iron phosphate battery

A simple model for discharge capacity of Ti-Mn based alloys

Capacity Degradation Prediction of Lithium-ion Battery Cycling with Various Protocols