Irradiation multi-scale damage and interface effects of 3D braided carbon fiber/epoxy composites subjected to high dose γ-rays
Shengkai Liu,Luyao Wang,Amna Siddique,Muhammad Umair,Chongyang Shi,Xiaoyuan Pei,Siqi Liu,Yue Yin,Haiting Shi,Zhiwei Xu
DOI: https://doi.org/10.1016/j.compositesb.2024.111575
IF: 11.322
2024-05-18
Composites Part B Engineering
Abstract:The serious damage caused to 3D braided carbon fiber (CF)/epoxy (EP) composites in high-energy irradiation environments is a pressing research topic that has not yet been reported. This study analyzed the γ-irradiation multi-scale damage of the matrix, interfaces, and near-interface regions in 3D braided CF/EP composites with three different braiding angles (18°, 28°, 38°) at atomic, microscopic, and macroscopic scales. The molecular structure and atomic charge information alterations of epoxy matrix were characterized using soft X-ray absorption spectroscopy (sXAS). When the irradiation dose reached 1000KGy, the compressive strength of composites decreased by 20.88%, 18.07%, and 16.60%, respectively, with an increase in the braiding angle. Micro-CT observation, along with statistical computing, confirmed that irradiation causes interface damage and increases the defect volume of 3D braided composites. Nanoindentation was used to compare the modulus of carbon fiber, interface, near-interface regions and matrix in irradiated composites and the function of CF/resin interface as an irradiation defect capture site in the irradiation resistance of resin-matrix composites has been newly established. In addition, the mechanism behind the effect of braiding angle on macroscopic properties was also analyzed.
engineering, multidisciplinary,materials science, composites