Mechanical properties and impact abrasive wear resistance in vanadium microalloyed medium carbon CrMo cast steel strengthened with nanoprecipitates
Long Zhao,Haining Liu,Xiangru Chen,Ganchao Zhai,Qijie Zhai
DOI: https://doi.org/10.1016/j.wear.2024.205679
IF: 4.695
2024-11-30
Wear
Abstract:The introduction of nanoprecipitates is highly effective in enhancing both strength and wear resistance of wear-resistant steels. In this study, the nanoprecipitates were introduced into medium carbon CrMo cast steel to improve mechanical properties and impact abrasive wear resistance. To control the density, size and distribution of nanoprecipitates generated through heat treatment, the vanadium was added. The effects of vanadium on impact abrasive wear resistance, along with their mechanical properties such as hardness, impact energy, and strength in medium carbon CrMo cast steel are systematically investigated. The results reveal that, compared to the V-free steel, the density of nanoprecipitates in the V-added steel increases from 0.89 × 10 12 /m 2 to 2.76 × 10 12 /m 2 , while the average diameter decreases to 92 nm, accompanied by a refinement of austenite grain size from 26.9 μm to 12.5 μm. The V-added steel exhibits a significant increase in yield strength (from 1450 MPa to 1630 MPa) and a decrease in impact energy (from 157 J to 127 J), while Rockwell hardness remains unchanged (53 HRC). This strengthening is mainly attributed to precipitation hardening and grain-boundary hardening induced by the addition of vanadium. Furthermore, the impact abrasive wear resistance of the V-added steel is enhanced by over one-fourth compared to V-free steel, which is attributed to the formation of a harder work-hardening layer. The wear mechanisms involve microploughing, microcutting, and a certain degree of surface fatigue, such as indentation, in medium carbon CrMo cast steel. However, with the introduction of vanadium, there is a notable decrease in the depths of microploughing, microcutting, and indentation.
engineering, mechanical,materials science, multidisciplinary