Abstract:Based on digital image correlation (DIC) technology and uniaxial compression tests, the deformation evolution characteristics of concrete were analyzed in the heating process under a sustained load and in the failure process under uniaxial compression. The effect of the sustained load on the mechanical properties of concrete at high temperatures was explored. A damage constitutive model of concrete under the combined action of high temperature and the sustained load was established. The research results show that a sustained load can effectively restrain the vertical thermal expansion of concrete and compact loose and weak zones of concrete. However, when the load level or temperature is too high, excessive lateral deformation of concrete will cause local strain concentration and cracking failure. In the failure process under uniaxial compression, both high temperature and sustained load can make the macroscopic cracks more smeared and branched. When the temperature is 200 C and 400 C, the sustained load has only a little enhancement effect on the high-temperature mechanical properties of concrete. When the temperature is 600 C and 800 C, the sustained load can significantly enhance the mechanical properties of concrete at high temperatures. However, at higher temperatures, excessive sustained loads can cause premature failure of the specimen. Based on the Weibull distribution, a statistical damage constitutive model of concrete under the combined action of sustained load and high temperature is established, which is in good agreement with the test curve. The curve of the degree of damage of concrete D-m shows that the sustained load causes the damage D-m to start earlier, the damage rate to increase, and the degree of damage at the peak stress to increase in the failure stage under uniaxial compression.

Mechanical Behavior and Constitutive Equation of Concrete under High-Temperature Dynamical Conditions

Experimental study on dynamic behavior of concrete at elevated temperatures

Strength of Concrete Filled Steel Tubes under High-Strain Rate Loading

Effect of High Temperature Exposure and Strain Rate on Mechanical Properties of High-Strength Steel Rebars

Finite element analysis of temperature effect and crack-control measures for ultra-long concrete structures

EXPERIMENTAL RESEARCH ON IMPACT BEHAVIOR OF CONCRETE-FILLED STEEL TUBE AT ELEVATED TEMPERATURES

Dynamic Tensile Properties and Energy Dissipation of High-Strength Concrete after Exposure to Elevated Temperatures

Study on the Constitutive Relationship between Ordinary Concrete and Nano-Titanium Dioxide-Modified Concrete at High Temperature

Investigating High-Temperature Deformation Evolution of Concrete under Sustained Loading Using DIC Technology and a Temperature-Mechanical Coupled Damage Constitutive Model

Experimental Investigation of the Static Expansion Tensile Behavior of Concrete after Exposure to Elevated Temperatures

Evaluation of Mechanical Properties of Concrete after Exposure to Elevated Temperatures Using Ultrasonic Pulse Velocity Measurement and a Split-Hopkinson Pressure Bar

CONSTITUTIVE MODEL OF HIGTH STRENGTH CONCRETE BEHAVIOUR AT HIGTH TEMPERATURES

Temperature-stress coupling constitutive relationship of concrete

Concrete Constitutive Relationships Under Different Stress-Temperature Paths

Combined effects of high temperature and high strain rate on normal weight concrete

Mechanical properties of concrete at high temperature—A review

Experimental Study on Damage Evaluation, Pore Structure and Impact Tensile Behavior of 10-Year-Old Concrete Cores After Exposure to High Temperatures

Investigation on Concrete-Pcm Interface under Elevated Temperature: at Material Level and Member Level

Stress–strain constitutive equations of concrete material at elevated temperatures

Dynamic Tensile Properties of Concrete under Different Environments

Dynamic Properties of Concrete under Severe Environmental Condition