Abstract:Concrete is a multiphase composite material consisting of aggregates, mortar, and initial defects. This work aims to quantitatively study the distribution and evolution of initial defects under elevated temperatures. To minimize the effect of hydration process and thermal and endogenous shrinkage, concrete samples cured in water for 12 months is tested. In order to study the effect of external load on the initial distribution of defects within concrete, concrete samples without pre-loading and pre-applied with 30% of the failure load are selected as research objects. The evolution of defects within the concrete samples are characterized using scanning electron microscopy (SEM). By employing an image processing software, the two-dimensional configurations of defects are extracted from the backscattered images obtained by SEM. Each defect is identified and approximated using an optimal ellipse. Thereafter, the defects are automatically recognized and classified into microcracks and pores by utilizing the image processing software and MATLAB programming. Consequently, the distribution and propagation of microcracks and pores in concrete could be quantitatively and separately analyzed. Statistical analysis of area, perimeter, and fitting ellipse parameters (e.g., major axis, minor axis, coordinates of the center, axis orientation, aspect ratio, and solidity) can provide the distribution of initial defects within concrete. It is demonstrated that the area of microcracks consistently increases with temperature. Log-normal and normal distributions may be suitable for the distribution of aspect ratio and solidity of microcracks, respectively, for both concrete samples with and without pre-applied loading under all elevated temperatures (40, 105, 150, 200, and 250 celcius). However, the distributions of area, coordinates of the center, and axis orientation of microcracks may vary with the initial concrete loading condition and temperature. For the pre-loaded concrete sample, the distribution of parameters does not conform to any type of distributions. Moreover, for the sample without pre-loading, the distributions of area, coordinates of the center, and axis orientation of microcracks exhibit good fitting precisions with log-normal, normal, and normal distributions, respectively at lower temperatures (40-150 celcius); however, such relationships do not apply at higher temperatures (200 and 250 celcius). As reference for identifying the variations in microstructures, 150 celcius is selected as the threshold temperature. The statistical approach employed in this study can lay the theoretical and experimental bases for determining the microstructure evolution in concrete. It can also be used for identifying the meso-defect and macro-defect and establishing their relationship with concrete properties. (c) 2021 Elsevier Ltd. All rights reserved.

Investigating High-Temperature Deformation Evolution of Concrete under Sustained Loading Using DIC Technology and a Temperature-Mechanical Coupled Damage Constitutive Model

Experimental study on dynamic behavior of concrete at elevated temperatures

Development of Internal Moisture Transfer and Cumulative Residual Strain in Concrete under Freeze-Thaw Cycles

Damage Based Constitutive Model for Predicting the Performance Degradation of Concrete

Experimental investigations and micromechanical thermal fatigue models of concrete

An Elastoplastic Damage Model for Concrete Subjected to Sustained High Temperatures

Study on the Constitutive Relationship between Ordinary Concrete and Nano-Titanium Dioxide-Modified Concrete at High Temperature

Experimental Study on Damage Evaluation, Pore Structure and Impact Tensile Behavior of 10-Year-Old Concrete Cores After Exposure to High Temperatures

Experimental Investigation of the Static Expansion Tensile Behavior of Concrete after Exposure to Elevated Temperatures

A novel multi-scale model for predicting the thermal damage of hybrid fiber-reinforced concrete

Influence of Flexural Loading on Chloride Ingress in Concrete Subjected to Cyclic Drying-Wetting Condition

Experimental and Analytical Investigation of Crack Spacing and Width for Overlaid RC Beams at Elevated Temperatures

Effect of High Temperature on Residual Mechanical Properties of Confined and Unconfined High-Strength Concrete

Dynamic tensile properties of thermally treated concrete specimens subjected to varied heating rates: an investigation using the digital image correlation method

Time-varying damage evolution of concrete under cyclic disturbance loading- an experimental observation utilizing AE and DIC

Statistical Damage Constitutive Model for High-Strength Concrete Based on Dissipation Energy Density

An elastoplastic damage constitutive model of concrete considering the effects of dehydration and pore pressure at high temperatures

Numerical modeling of delayed damage and failure of concrete structures under sustained loading

Dynamic Tensile Properties and Energy Dissipation of High-Strength Concrete after Exposure to Elevated Temperatures

A length scale insensitive phase‐field model for fully coupled thermo‐mechanical fracture in concrete at high temperatures

Statistical Analysis of Defects Within Concrete under Elevated Temperatures Based on SEM Image