Abstract:To investigate the durability of cementitious materials under complex environmental conditions in Xinjiang, this study conducted durability tests on mortar specimens with different fly ash contents under dry/wet sulfate attack conditions, with standard curing and steam curing at 70 °C. The appearance loss and flexural and compressive strength variations in the specimens were analyzed, and an evolution model of the mortar strength under a dry/wet sulfate attack was established. Moreover, XRD and SEM techniques were used to characterize the erosion products and microstructure, and to explore the erosion resistance mechanism of fly ash cementitious materials. The results showed that, after 160 cycles of erosion, the flexural strength of the specimens decreased with the increase in the fly ash content. In the context of steam-cured mortar specimens, throughout the entire erosion period, specimens with a fly ash content of 45% exhibited the highest relative compressive strength. The established strength evolution model had a minimum determination coefficient of 0.879, indicating a good agreement between the model and experimental results. Microscopic research showed that fly ash would undergo a pozzolanic reaction under the action of sulfate and calcium hydroxide, which was beneficial to the improvement of the erosion resistance. As the fly ash content increased, the erosion products of the specimens gradually became dominated by gypsum.

Development of Cementitious Materials with High Resistance to Sulfate Attack by A Combination of Emulsified Asphalt and Fly Ash

Experiment on Cement-Based Materials with Various Compositions Against Sulfate Attack

Effect of Mineral Admixtures on Sulfate Attack Resistance of Cement-Based Materials

Investigating the sulfate resistance of mortars with multiple mineral admixtures in ammonium-magnesium sulfate solution

Experimental Investigation On Mineral Admixture In Improving The Properties Of Concrete To Sulfate Attack

Deterioration behaviors of sulfate crystallization attack on cement-based material

Degradation mechanism of cement mortar exposed to combined sulfate–chloride attack under cyclic wetting–drying condition

Properties evolution of calcium sulfoaluminate cement blended with ground granulated blast furnace slag suffered from sulfate attack

Research on the Sulfate-resistant Chemical Attack Mechanism of Concrete with Mineral Admixture

Deterioration Mechanism of Plain and Blended Cement Mortars Partially Exposed to Sulfate Attack

Evaluating Deterioration of Concrete by Sulfate Attack

Resistance Against Sulfate Attack of Cement Mortar Blended with Ultrafine Slag Powder

Deterioration Evolutive Process of Cement-Based Materials under Sulphate Physical Crystallization Attack

Sulfate Crystallization Attack on Cement-Based Materials

Effects and Mechanisms of Mineral Admixtures on Sulfate Attack of Cement Mortars

Sulfate attack on concrete with mineral admixtures

Influence of Fly Ash Content on the Durability of Mortar Specimens under Dry/Wet Sulfate Attack

Experimental Study and Evaluation of Bonding Properties Between Fiber and Cement Matrix under Sulfate Attack

Sulfate Attacks on Uncarbonated Fly Ash + Cement Pastes Partially Immersed in Na2SO4 Solution.

DURABILITY OF LOW STRENGTH CONCRETE WITH HIGH VOLUME FLY ASH SUBJECTED TO SULFATE ATTACK

Influence of Cement Types and Mineral Admixtures on Resistance of Mortar to Sulfate Attack under Lower Temperature