Abstract:Polycrystalline Ni3Al-based superalloy with up to 70% <math>γ′</math> phase owns excellent strength at around 1100 °C. It has been successfully used as a substitute for turbine blade crown, which is one of the aircraft components working in the severest environment (i.e., sometimes nearly overheating). However, few studies concentrate on the coarsening resistance and phase thermal stability in this newly designed polycrystalline superalloy at the working temperature, hence, directional coarsening behavior of primary <math>γ′</math> <math>(γI′)</math> has remained restricted. This paper investigated directional coarsening behavior of <math>γI′</math> during aging treatment (1100 °C) after overheating at 1270 °C with furnace cooling (SFA), air cooling (SAA) and water cooling (SWA) respectively. It clearly showed that <math>γI′</math> grew into lamellar and gradually became irregular during the directional coarsening process. Moreover, its morphological combination mode was illustrated. Since parallel short lamellar <math>γI′</math> connected each other, long lamellar formed. When perpendicular long lamellar <math>γI′</math> connected each other, it became L-type or T-type, i.e., precursor of irregular <math>γI′</math>. The kinetics of directional coarsening regime of <math>γI′</math> was in line with the matrix-diffusion-controlled (MDC) theory according to the evaluation of <math>γI′</math> size. This was caused by higher migration of <math>γI′</math> interfaces than the diffusion of solute elements. It was also confirmed that driving force of directional coarsening mainly depended on the competition of elemental diffusion, lattice misfit distribution and <math>γ</math> channel distance.

Microstructure and Mechanical Property of a Directional Ni-Based Superalloy During Long-Term Exposure

Microstructure Degradation of Service-Exposed Turbine Blades Made of Directionally Solidified DZ125 Superalloy

Carbide Evolution of a Directionally Solidified Ni-Based Superalloy During Long-Term Exposure

Dependence of Microstructural Evolution on the Geometric Structure for Serviced DZ125 Turbine Blades

Mechanical Degradation Behavior and Γ′ Coarsening Mechanism of a Ni-based Superalloy During Long-Term High-Temperature Thermal Exposure

Effects of Long-Term Aging on the Microstructures and Tensile Properties of Ni-Based Single Crystal Superalloy

Microstructure Characterization of Ni-Based Superalloys During Thermal Exposure

Study on the Microstructure and Mechanical Property Degradation of Ni-Based Superalloy in Long-Term Service

Vibration Fatigue Behavior and Life Prediction of Directionally Solidified Superalloy Based on the Phase Transformation Theory

Mechanism of High Temperature Mechanical Properties Enhancement of Ni-based Superalloys Repaired by Laser Directed Energy Deposition: Microstructure Analysis and Crystal Plasticity Simulation

Thermomechanical Fatigue Experimental Study on a Notched Directionally Solidified Ni-base Superalloy

Experimental Investigation and Modelling of Microstructure Degradation in a DS Ni-based Superalloy Using a Quantitative Cross-Correlation Analysis Method

Investigation of Microstructural Stability and Tensile Deformation Behavior of a Novel PM Ni-based Superalloy During Long-Term Thermal Exposure

Microstructure and Tensile Behavior of Nickel-Based Single Crystal Superalloys with Different Re Contents

Influence of thermal exposure on microstructural stability and tensile properties of a new Ni-base superalloy

Processing, Microstructures and Mechanical Properties of a Ni-Based Single Crystal Superalloy

The microstructure evolution and its effect on the mechanical properties of a hot-corrosion resistant Ni-based superalloy during long-term thermal exposure

Microstructural Evolution and Mechanical Properties of a Nickel-Based Superalloy Through Long-Term Service

Directional coarsening behavior of primary γ′ phase in Ni3Al-based superalloy during aging heat treatment

Microstructure and mechanical degradation of K403 Ni-based superalloy from ultra-long-term serviced turbine blade

Effects of Long Term Thermal Exposure on Microstructure and Mechanical Property Evolution of a New Wrought Ni–Fe Based Superalloy