Abstract:The rust/metal structure is one of the multiphase and multiple interface complex systems. The corrosion under rust is the uppermost and longest form of metallic corrosion evolution process. It is difficult to accurately determine the electrochemical parameters because the existence of rust complicates the electrochemical corrosion process. Based on the result of the previous studies of quiescent seawater, the weight-loss method and different electrochemical tests such as polarization curves (PC), electrochemical impedance spectra (EIS) and linear polarization resistance (LPR) were carried out to study the corrosion behavior of A3 carbon steel immersed in flowing seawater for about 280 d. After very short immersing time, there is a thin yellow rust layer on carbon steel, but as time prolonged, the yellow corrosion products are rushed away quickly, and a tense black rust layer cover about the whole electrode. The corrosion rate obtained by weight-loss method show a steady decline and keep stable after about 84 d, but it is higher than that of the static state system data. The cathodic polarization curves show an obvious reduction current peak at about -950 mV, which makes a remarkable overestimating of the cathodic corrosion current. Polarization resistance (R-p), determined by LPR and EIS, increases during the merely short-initial immersion period, then, it decreases gradually with immersion time. This means that the corrosion rate determined by electrochemical tests shows an another pattern compared with the weight-loss result. After a very short immersion time (about 14 d), there is a remarkable deviation between the weight-loss and electrochemical test results, and the longer immersed the greater of this deviation is. So no matter in static state or flowing seawater, electrochemical methods can not get an accurate corrosion rate of carbon steel. And reliable electrochemical measurement and analysis for rusted steel need much more attention.

Study on the Flow- Induced Corrosion of P110 Oil Tube with an Electrochemical Method

Effect of Flow Rate on the Corrosion Behavior of P110 Steel in High-Ca2+ and High-Cl− Environment

Influences of temperature on corrosion behavior of P110 steel

Research of CO_2 Corrosion Kinetics of Tubing and Casing Steel P110

Corrosion Behavior of Oil Tube Steels under Conditions of Multiphase Flow Saturated with Super-Critical Carbon Dioxide

Flow-Assisted Corrosion of API 5L X56 Steel: Effect of Flow Velocity and Dissolved Oxygen

Experimental and Numerical Investigation into the Corrosion Performance of X100 Pipeline Steel under a Different Flow Rate in CO2-saturated Produced Water

Study on corrosion behavior of P110S steel in CO2-H2S- saturated solution

On-Line Measurement and Characterization of Electrochemical Corrosion of 304L Stainless Steel Pipe Wall in High-Speed Cl-Containing Solution

Effect of Temperature on CO2/H2S Corrosion Rate of Oil Tube Steels

Electrochemical Behavior in Erosion- Corrosion of Carbon Steel in Liquid-Solid Double Phase Flow Loop

Experimental Study on Corrosion Performance of Oil Tubing Steel in HPHT Flowing Media Containing O2 and CO2

Internal localized corrosion of X100 pipeline steel under simulated flow conditions

Effects of Temperature on Galvanic Corrosion Behaviors of Super 13Cr and P110 Steel Couples in NaCl Solution

Microstructural Understanding of Flow Accelerated Corrosion of SA106B Carbon Steel in High-Temperature Water with Different Flow Velocities

Electrochemical Investigation of Chloride Ion-Induced Breakdown of Passive Film on P110 Casing Steel Surface in Simulated Pore Solution: Behavior and Critical Value Determination

Corrosion Behavior of WB36CN1 Steel at Different Flow Rates

STUDY OF THE X70 PIPELINE STEEL CORRODING IN 3.0wt% NaCl SOLUTION USING ELECTROCHEMICAL IMPEDANCESPECTROSCOPY TECHNIQUE

Corrosion Behavior of J55 Steel in Oilfield Water

Corrosion Behavior of Long-Time Immersed Rusted Carbon Steel in Flowing Seawater

Electrochemical Corrosion Behaviors of 316 L Stainless Steel Used in PWR Primary Pipes