Physical properties of transparent perovskite oxides (Ba,La)SnO3 with high electrical mobility at room temperature
Hyung Joon Kim,Useong Kim,Tai Hoon Kim,Jiyeon Kim,Hoon Min Kim,Byung-Gu Jeon,Woong-Jhae Lee,Hyo Sik Mun,Kwang Taek Hong,Jaejun Yu,Kookrin Char,Kee Hoon Kim
DOI: https://doi.org/10.48550/arXiv.1207.0764
2012-07-03
Materials Science
Abstract:Transparent electronic materials are increasingly in demand for a variety of optoelectronic applications. BaSnO3 is a semiconducting oxide with a large band gap of more than 3.1 eV. Recently, we discovered that La doped BaSnO3 exhibits unusually high electrical mobility of 320 cm^2(Vs)^-1 at room temperature and superior thermal stability at high temperatures [H. J. Kim et al. Appl. Phys. Express. 5, 061102 (2012)]. Following that work, we report various physical properties of (Ba,La)SnO3 single crystals and films including temperature-dependent transport and phonon properties, optical properties and first-principles calculations. We find that almost doping-independent mobility of 200-300 cm^2(Vs)^-1 is realized in the single crystals in a broad doping range from 1.0x10^19 to 4.0x10^20 cm^-3. Moreover, the conductivity of ~10^4 ohm^-1cm^-1 reached at the latter carrier density is comparable to the highest value. We attribute the high mobility to several physical properties of (Ba,La)SnO3: a small effective mass coming from the ideal Sn-O-Sn bonding, small disorder effects due to the doping away from the SnO2 conduction channel, and reduced carrier scattering due to the high dielectric constant. The observation of a reduced mobility of ~70 cm^2(Vs)^-1 in the film is mainly attributed to additional carrier-scatterings which are presumably created by the lattice mismatch between the substrate SrTiO3 and (Ba,La)SnO3. The main optical gap of (Ba,La)SnO3 single crystals remained at about 3.33 eV and the in-gap states only slightly increased, thus maintaining optical transparency in the visible region. Based on these, we suggest that the doped BaSnO3 system holds great potential for realizing all perovskite-based, transparent high-frequency high-power functional devices as well as highly mobile two-dimensional electron gas via interface control of heterostructured films.