Abstract:In this study, a novel sol-gel method is used to synthesize amorphous silica-alumina materials with a narrow mesoporous distribution and various Si/Al molar ratios without using any templates and pore-regulating agents. During the preparation procedure, only inexpensive inorganic salts were used as raw materials, instead of expensive and harmful alkoxides. The precursor sol was dried at room temperature in a vacuum box kept at 60 mmHg until it began to form the gel. The results of a nitrogen sorption experiment indicate that the synthesized materials with different Si/Al molar ratios have similar mesoporous distributions (within 2-12 nm). Moreover, it was found that the material's pore size distribution remains at a similar value during the heat treatment from room temperature to 550 degreesC. On the basis of the nitrogen sorption, TEM, and AFM characterization results, a formation mechanism of mesopores which accounts for the experimental data is also suggested. This suggested mechanism involves rearrangement of the primary particles during the drying process to form the precursors of the similarly sized mesopores. The synthesized materials were characterized by XRD, thermal analysis (TG/DTA), Al-27 and Si-29 MAS NMR spectroscopy, SEM, TEM, and AFM. The results of Al-27 and 29Si MAS NMR indicate that the distribution of silicon and aluminum in the synthesized materials is more uniform and homogeneous than that in the mixed oxides prepared via the traditional sol-gel method even at high alumina contents. The type and density of the acid sites were studied using pyridine adsorption-desorption FTIR spectroscopy. It was shown that the acidity of the synthesized materials is higher than that of the silica-alumina materials prepared by conventional methods.

Vapor phase synthesis of mesoporous silica rods within the pores of alumina membranes

Hierarchically Structured Periodic Mesoporous Silica by Vapor Phase Synthesis

Direct Synthesis of Mesoporous Carbon Microwires and Nanowires

Preparation of high-performance zeolite NaA membranes in clear solution by adding SiO2 into Al2O3 hollow-fiber precursor

Ultrasonic Synthesis of Silica−Alumina Nanomaterials with Controlled Mesopore Distribution Without Using Surfactants

A Novel Method To Synthesize Amorphous Silica−Alumina Materials with Mesoporous Distribution without Using Templates and Pore-Regulating Agents

The preparation of zeolite NaA membranes on the inner surface of hollow fiber supports

Morphological Characterization of γ-Al 2 O 3 Membranes Fabricated from Ammonium Aluminum Sulphate

Preparation of Asymmetric Zeolite NaA Membrane Layers by Vapor Phase Transfer and Seeded Growth Method

Preparation of Zeolite NaA Membranes on Macroporous Alumina Supports by Secondary Growth of Gel Layers

Synthesis of mesoporous silica hollow spheres in supercritical CO2/water systems

Ultrasound As a Tool to Synthesize Nano-Sized Silica–Alumina Catalysts with Controlled Mesoporous Distribution by a Novel Sol–Gel Process

Sol-Gel Synthesis of Nano-Sized Silica-Alumina Mesoporous Molecular Sieves with Bimodal Pore Structure

Synthesis of Nanometer-sized Mesoporous Silica and Alumina Spheres

Synthesis of nanoporous Al2O3 membranes from polybutyl methacrylate functionalized SiO2 particles as a sacrificial template

Synthesis and characterization of mesoporous silica membranes via dip-coating and hydrothermal deposition techniques

Novel vesicular mesoporous material templated by catanionic surfactant self-assembly

Structural Characterization of Mesoporous Silica Nanofibers Synthesized Within Porous Alumina Membranes

Control of morphology in synthesizing mesoporous silica

An Efficient Synthesis of NaA Zeolite Membranes from Direct Crystallization of Gel-Dipped Macroporous Alumina Tubes with Seeds

Mesoporous silica-coating of gold nanorods by a templated method