Abstract:This work investigates the heterogeneous deformation and failure of HR3C austenitic stainless steel welded joints at room and typical service temperatures. Such types of welded joints are widely used in the new generation of fossil fuel power stations and are known to suffer from premature high temperature failure. Observation of in-service failures revealed that cracks may nucleate either in the heat affected zone or in the weld metal. The main objective of this work is to identify the local microstructural conditions and stress–strain fields responsible for both ductile failure and micro-crack nucleation within the weldment at low and high temperatures, respectively. To that purpose, a novel multi-scale micromechanics-based modelling framework is proposed. It relies on representative weld microstructure models digitally reconstructed from EBSD measurements, and dislocation density-based crystal plasticity models to describe the behaviour of individual grains in each weld region. A novel thermo-dynamically consistent relation for the configuration stored energy per unit volume is derived from the crystal plasticity framework. The single crystal models are calibrated and validated from a combination of uniaxial tensile tests on cross-weld specimens using high resolution digital image correlation techniques, representative volume elements of the polycrystals at the macro-scale, as well as micropillar compression tests at the scale of the individual grains. Predictions of heterogeneous inelastic deformation fields within the weldment at both 22 °C and 665 °C, and of micropillar compression behaviour of the individual weld single crystal phases are consistent with experimental data. The experimentally observed ductile failure of the weld metal at room temperature is successfully predicted using a Gurson-type void nucleation, growth and coalescence constitutive model. The suitability of the stored strain energy density and the accumulated plastic strain as crack initiation/creep failure indicators is investigated. It was found that predicted creep lifetimes with either indicator were very similar, and that they were relatively accurate for low stress levels.

Prediction of Vulnerable Zones Based on Residual Stress and Microstructure in CMT Welded Aluminum Alloy Joint

Prediction of the Ultra-Low-Cycle Fatigue Damage of Q345qC Steel and Its Weld Joint

Low Cycle Fatigue Properties and Fracture Mechanism of Q345qC Steel and Its Welded Joint

Study on the Prediction Method of the Ultra-Low-Cycle Fatigue Damage of Steel

Residual Stress Modeling of Narrow Gap Welded Joint of Aluminum Alloy by Cold Metal Transferring Procedure

An Insight into the Creep-Fatigue Damage Localization in Welded Joints Based on Crystal Plasticity Finite Element Method

Numerical Simulation of Residual Stresses in Multipass Gas Metal Arc-Welded Joints of Thick Aluminum Alloy Plates

Investigation of the Mesoscale Damage Evolution Process of AA5754O Aluminum Alloy CMT Welded Joints

Predicting Welding Residual Stress of a Multi-pass P92 Steel Butt-Welded Joint with Consideration of Phase Transformation and Tempering Effect

Effect of softening of 6082-T6 aluminum alloy CMT welded joints on mechanical properties and fracture behavior

Strength calculation and microstructure characterization of HAZ softening area in 6082-T6 aluminum alloy CMT welded joints

Fracture prediction in transverse fillet welded joints of high strength structural steel

Numerical and experimental study on thermal-metallurgical-mechanical behavior of high-strength steel welded joint

Influence of Material Model on Prediction Accuracy of Welding Residual Stress in an Austenitic Stainless Steel Multi-pass Butt-Welded Joint

Micro-mechanics investigation of heterogeneous deformation fields and crack initiation driven by the local stored energy density in austenitic stainless steel welded joints

Study of Microstructure and Stress Corrosion Cracking Behavior in Welding Transition Zone of Ni-Based Alloys

Microstructure and pore sensitivities in very high cycle fatigue behaviors of titanium alloy welded joints under stress ratios

Experimental Investigation of Fatigue Behaviour for Welded Joint with Mechanical Heterogeneity

Strength Mismatch Effect on Residual Stress of High Strength Steel Butt-Welded Joints

Numerical simulation on interfacial creep failure of dissimilar metal welded joint between HR3C and T91 heat-resistant steel

Study of Microstructure and Fatigue in Aluminum/Steel Butt Joints Made by CMT Fusion-Brazing Technology