Abstract:Porous materials with high specific surface area, high porosity, and high electrical conductivity are promising materials for functional applications, including catalysis, sensing, and energy storage. Molten salt dealloying was recently demonstrated in microwires as an alternative method to fabricate porous structures. The method takes advantage of the selective dissolution process introduced by impurities often observed in molten salt corrosion. This work further investigates molten salt dealloying in bulk Ni–20Cr alloy in both KCl–MgCl 2 and KCl–NaCl salts at 700 °C, using scanning electron microscopy, energy dispersive spectroscopy, and X-ray diffraction (XRD), as well as synchrotron X-ray nano-tomography. Micro-sized pores with irregular shapes and sizes ranging from sub-micron to several microns and ligaments formed during the process, while the molten salt dealloying was found to progress several microns into the bulk materials within 1–16 h, a relatively short reaction time, enhancing the practicality of using the method for synthesis. The ligament size increased from ~ 0.7 μm to ~ 1.3 μm in KCl–MgCl 2 from 1 to 16 h due to coarsening, while remaining ~ 0.4 μm in KCl–NaCl during 16 h of exposure. The XRD analysis shows that the corrosion occurred primarily near the surface of the bulk sample, and Cr 2 O 3 was identified as a corrosion product when the reaction was conducted in an air environment (controlled amount sealed in capillaries); thus surface oxides are likely to slow the morphological coarsening rate by hindering the surface diffusion in the dealloyed structure. 3D-connected pores and grain boundary corrosion were visualized by synchrotron X-ray nano-tomography. This study provides insights into the morphological and chemical evolution of molten salt dealloying in bulk materials, with a connection to molten salt corrosion concerns in the design of next-generation nuclear and solar energy power plants.

Evolution of Porous Structure with Dealloying Corrosion on Gasar Cu–Mn Alloy

Evolution mechanisms and kinetics of porous structures during chemical dealloying of binary alloys

Evolution of Nanoporosity in Dealloying

Synthesis and mechanical properties of porous metals with inverted dealloying structure

Porosity evolution and oxide formation in bulk nanoporous copper dealloyed from a copper-manganese alloy studied by in situ resistometry

Fabrication of a Three-Dimensional Bimodal Porous Metal

Fabrication of Nanoporous Metal by Selective Electrochemical Dealloying from Laser Cladding Cu-Mn Alloys

Effects of Alloying Element and Pore Structure on Mechanical Property and Corrosion Properties of Gasar Mg Alloys

Electrochemical Impedance Spectra for the Corrosion of Porous Cu-35mass%Ni-(5,10)mass%Cr Alloys in Molten (0.62li,0.38k)2co3 at 650 °C in Air

Fabrication and Characterization of Nanoporous Manganese Structure by Laser Deposition Hybrid Selective Electrochemical Dealloying

Evolution of micro-pores in Ni–Cr alloys via molten salt dealloying

Microstructure-dependent oxidation-assisted dealloying of Cu0.7Al0.3 thin films

Preparation of nanoporous copper foil by chemical dealloying from electro-deposited CuZn alloy

Influence of the Solidification Temperature Range on Gasar Structures Made from Cu–Mn Alloys

Rapid preparation of micro/nano porous Cu/Cu 2 O particles through dealloying of powder sintered Cu-Al alloy

Compressive and Corrosion Properties of Lotus-Type Porous Mg-Mn Alloys Fabricated by Unidirectional Solidification

Experimental Study on the Pore Structure of Directionally Solidified Porous Cu-Mn Alloy

A Study of Electroplated Nanoporous Copper Using Aberration-Corrected Transmission Electron Microscopy

Dealloying to Nanoporous Au/Pt Alloys and Their Structure Sensitive Electrocatalytic Properties.

Formation and characterization of Monolithic nanoporous copper by chemical dealloying of Al-Cu alloys

Fabrication and Functionalization of Tunable Nanoporous Copper Structures by Hybrid Laser Deposition and Chemical Dealloying