Formation and properties of biocompatible Ti-based bulk metallic glasses in the Ti–Cu–Zr–Fe–Sn–Si–Ag system
Wei Yang,Ying Liu,Nengbin Hua,Shujie Pang,Yan Li,Peter K. Liaw,Tao Zhang
DOI: https://doi.org/10.1016/j.jnoncrysol.2021.121060
2021-11-01
Abstract:<p>The Ni-free Ti-based bulk metallic glasses (BMGs) with high glass-forming ability (GFA) can be synthesized in the (Ti, Cu, Zr)<sub>92.5</sub>Fe<sub>2.5</sub>Sn<sub>2</sub>Si<sub>1</sub>Ag<sub>2</sub> alloy system over a wide composition range by copper-mold casting. Especially, the Ti<sub>48</sub>Cu<sub>37</sub>Zr<sub>7.5</sub>Fe<sub>2.5</sub>Sn<sub>2</sub>Si<sub>1</sub>Ag<sub>2</sub> glassy alloy can form the BMG rod with a diameter up to 6 mm and showed a high compressive strength of ~ 2.05 GPa, elastic modulus of ~ 100 GPa, and microhardness of ~ 571 Hv. The Ti-based BMGs presented good bio-corrosion resistance in a simulated physiological environment attributed to the formation of Ti-, Zr-, Si-, and Fe-enriched passive films. The biocompatibility of the Ti-based glassy alloys was systematically investigated by both indirect cytotoxicity test and direct cell-culture experiments. The Ti-based BMG extracts had no cytotoxic effects on the proliferation of the cells. The good cell adhesion, proliferation, differentiation, and mineralization of bone-forming MC3T3-E1 pre-osteoblasts on the BMGs were parallel to those on the Ti–6Al–4V alloy. These results manifested that the present Ti-based BMGs are promising candidates as biomaterials.</p>
materials science, multidisciplinary, ceramics