Abstract:Activated carbon is widely used to purify flue gas in industries like steel and metallurgy, but its ability to adsorb NOx at medium to low flue gas temperatures is limited. This study conducted adsorption experiments in different atmospheres within -20 to 30 degrees C. As the temperature decreased from 30 degrees C to -20 degrees C, the NOx adsorption amount was increased by 4.61 times. Lowering temperature greatly promoted NOx adsorption. Temperatureprogrammed desorption experiments determined the amount of NOx adsorbed through physical adsorption and chemical adsorption. As the temperature decreased from 30 degrees C to -20 degrees C, the proportion of physically adsorbed NOx to total adsorption amount increased from 2.9 % to 45.5 %, and the proportion of physically adsorbed NO2 to total physical adsorption amount increased from 0 to71.6 %. Lowering the temperature benefited NO oxidation and NO2 ' s adsorption on activated carbon. Desorption curves of chemically adsorbed NOx indicated that a decrease in temperature does not affect the chemical adsorption pathways of NOx. Physical adsorption of NOx was studied by density functional theory calculations. NO2 has much stronger physical adsorption than NO and can physically adsorb near saturated carbon atoms, carbonyl groups, ether groups, hydroxyl groups, and lactone groups. At low temperatures, NO is first oxidized to NO2 on activated carbon and then NO2 is adsorbed through both physical and chemical pathways. Modifying the surface of activated carbon to increase hydroxyl, ether, and lactone groups can help enhance its performance of low-temperature NOx adsorption.

NH3-activated Carbon Nanofibers for Low-Concentration NO Removal at Room Temperature

Room Temperature Nox Removal Over Carbon Nanofibers Fabricated By Electrospinning

Preparation of Porous Carbon Nanofibers with Controllable Pore Structures for Low-Concentration NO Removal at Room Temperature

NO removal by electrospun porous carbon nanofibers at room temperature

Nitrogen Doping of Activated Carbon Loading Fe2O3 and Activity in Carbon-Nitric Oxide Reaction

Catalytically oxidation of NO into NO2 at room temperature by graphitized porous nanofibers

Low-temperature Selective Catalytic Reduction of NO with NH3 over Nanoflaky MnOx on Carbon Nanotubes in Situ Prepared Via a Chemical Bath Deposition Route

Nitrogen-Doped Pitch-Based Activated Carbon Fibers with Multi-Dimensional Metal Nanoparticle Distribution for the Effective Removal of NO

High-efficiency NO electroreduction to NH3 over honeycomb carbon nanofiber at ambient conditions

Effect of Nitrogen Doping on the Reduction of Nitric Oxide with Activated Carbon in the Presence of Oxygen

Low-Temperature Reduction of NOx by NH3 with Unity Conversion on Nanofilament MnO2/Activated Semi-Coke Catalyst

Adsorption and Reduction of NO2 over Activated Carbon at Low Temperature

Activated Carbon Fibers Loaded with MnO2 for Removing NO at Room Temperature

The Effect of the NH3 Activation Temperature of Graphene/carbon Composite Nanofibers on Their NO Catalytic Oxidation Performance at Room Temperature

Modifying Porous Carbon Nanofibers with MnOx–CeO2–Al2O3 Mixed Oxides for NO Catalytic Oxidation at Room Temperature

Co–NCNT nanohybrid as a highly active catalyst for the electroreduction of nitrate to ammonia

Efficient electrochemical NO reduction to NH<sub>3</sub> over metal-free g-C<sub>3</sub>N<sub>4</sub> nanosheets and the role of interface microenvironment

Characteristics and Mechanism of Low-Temperature NO Adsorption by Activated Carbon

Efficient electrochemical NO reduction to NH3 over metal-free g-C3N4 nanosheets and the role of interface microenvironment

Low Temperature Selective Catalytic Reduction of NO and NO2 with NH3 over Activated Carbon-Supported Vanadium Oxide Catalyst

Selective catalytic reduction of NO with NH3 over CuOX-carbonaceous materials