Abstract:TiAl alloy is one of the most attractive candidates for a new generation of high-temperature structural materials and has broad application prospects in the aerospace field. As a typical intermetallic material, TiAl is inevitably difficult to process using conventional methods. Election beam selective melting (EBSM) is an effective method of addictive manufacturing to prepare TiAl alloy with a complex structure. However, the microstructure of TiAl alloy formed using EBSM often contains defects such as pores, which seriously reduces the mechanical properties of the material. In this work, the effects of EBSM and post-processing procedures on the microstructure and mechanical properties of Ti-48Al-2Cr-2Nb alloy were studied. The results show that the microstructure of Ti-48Al-2Cr-2Nb alloy formed using the EBSM process was dense and composed of equiaxed γ-phase and double-phase regions. A large number of dislocations that formed due to thermal stress were clearly observed inside the Ti-48Al-2Cr-2Nb alloy. When the EBSM process parameters were 13.5 mA, 4.0 m/s, and 40.50 J/mm3, as the current intensity increased, the Al content decreased, the content of α2 phase increased, and the microstructure of the material was coarse. The results of the tensile test fracture morphology indicate that the Ti-48Al-2Cr-2Nb alloy exhibited brittle fracture during tensile deformation, lacking the typical yield deformation of metal materials. As the energy density of the EBSM process increased, the mechanical properties of the Ti-48Al-2Cr-2Nb alloy first increased and then decreased. The samples prepared with an energy density of 34.50~40.50 J/mm3 had excellent mechanical properties, of which the maximum tensile strength and maximum elongation reached 643 MPa and 2.09%, respectively. The phase composition of the Ti-48Al-2Cr-2Nb alloy after hot isostatic pressing (HIP) treatment remained unchanged from the EBSM samples, but there was a slight difference in content. There was an increase in the amount of γ phase and a decrease in B2 phase, accompanied by the generation of a massive γ phase after HIP treatment. Moreover, the number of dislocations inside the material increased. The Ti-48Al-2Cr-2Nb alloy after HIP treatment exhibited obvious plastic deformation characteristics, with a tensile strength of 679 MPa and elongation of 2.5%. A heat treatment of 900 °C/5 h was performed on the Ti-48Al-2Cr-2Nb alloy after HIP. The dislocation density of the Ti-48Al-2Cr-2Nb alloy decreased, and the B2 phase transformed from massive to lamellar.

The microstructures and properties of an al- 12 wt pct

Microstructures and Tensile Properties of an A1-12 Wt Pct Si Alloy Produced by Reciprocating Extrusion

Microstructure and Mechanical Properties of Selective Laser Melted Mg-9 Wt%al Powder Mixture

Microstructures and Mechanical Properties of a L12-structured Precipitation Strengthened Co-based Superalloy

Effect of Processing Route on Microstructure and Mechanical Properties of an Al-12Si Alloy

Microstructure and mechanical properties of Al-Mg-Si alloy fabricated by a short process based on sub-rapid solidification

An Improved Process for Solving the Sintering Problem of Al-Si Alloy Powder Metallurgy

A study of the microstructures and properties of an A390.0 aluminium alloy produced by the layer deposition process

Microstructures Of Components Synthesized Via Electron Beam Selective Melting Using Blended Pre-Alloyed Powders Of Ti6al4v And Ti45al7nb

Heterogeneous microstructure and mechanical behaviour of Al-8.3Fe-1.3V-1.8Si alloy produced by laser powder bed fusion

Microstructure and mechanical properties of Al-Mg-Si alloy during solution heat treatment and forging integrated forming process

Developing a high-strength Al-Mg-Si-Sc-Zr alloy for selective laser melting: Crack-inhibiting and multiple strengthening mechanisms

Microstructure and Mechanical Properties of Al-Si Alloys Produced by Rapid Solidification and Hot Extrusion

Microstructural evolution and strengthening mechanism of high-strength AlSi8.1 Mg1.4 alloy produced by selective laser melting

TiAl Alloy Fabricated Using Election Beam Selective Melting: Process, Microstructure, and Tensile Performance

Microstructure and Coefficient of Friction of Silumins Obtained by Rapid Solidification

Effect of process parameters on microstructures and properties of Al-42Si alloy fabricated by selective laser melting

Fe-bearing phase formation, microstructure evolution, and mechanical properties of Al-Mg-Si-Fe alloy fabricated by the twin-roll casting process

Selective laser melting processing of heterostructured Ti6Al4V/FeCoNiCrMo alloy with superior strength and ductility

Periodic Microstructure of Al–Mg Alloy Fabricated by Inter-Layer Hammering Hybrid Wire Arc Additive Manufacturing: Formation Mechanism, Microstructural and Mechanical Characterization

Effects of Fe-6.5wt.%Si alloys prepared by different cooling methods on ordered structure and mechanical properties