Fabrication of Al/Al-TiB 2 laminate composites via hot press sintering process: An insight into the mechanical properties and fracture behavior
Biaohua Que,Liang Chen,Yongjun Chen,Lihua Qian,Guoqun Zhao,Cunsheng Zhang
DOI: https://doi.org/10.1016/j.jmapro.2023.11.040
IF: 5.684
2023-12-12
Journal of Manufacturing Processes
Abstract:The Al/Al-TiB 2 laminated composites with different numbers of layers was fabricated by hot press sintering method. The results show that Al/Al-TiB 2 interface is well bonded without obvious micropores , cracks, or other defects, while the stacking faults and dislocation loops are observed at the interface. The average grain sizes of Al and Al-TiB 2 layers are 45.17 and 5.51 μm in the composite with 3 layers, while they greatly increase to 80.07 and 6.51 μm in the composite with 5 layers. The hardness increases gradually along Al layer, Al/Al-TiB 2 interface, and Al-TiB 2 layer. TiB 2 particles mainly contributes to the enhancement of bending strength, and the maximum strength of 110.0 MPa is achieved in the composite with 3 layers due to the fine grain size, small particle spacing, and more geometrically necessary dislocations in Al-TiB 2 layer. During bending deformation, Al layer exhibits ductile fracture with shear lip, slip band, fatigue striation and dimple, while Al-TiB 2 layer shows typical brittle fracture with micro-voids and cleavage. The stress concentration and crack always appear in Al-TiB 2 layer, while Al layer can transfer strain and inhibit strain localization . An increasing ductility of the laminated composites is achieved due to crack deflection, interfacial delamination, and strain transferring.
engineering, manufacturing