Abstract:The morphological evolution and grain orientations of intermetallic compounds (IMCs) were investigated during the formation of full Cu3Sn joints at two soldering temperatures (310 and 430 °C). The mechanical properties of both types of full Cu3Sn joints were then analyzed. The experimental results showed that the morphology of interfacial IMCs varied significantly at two temperatures. At 310 °C, scallop-like Cu6Sn5 grains became larger but were fewer in number and the top of the scallops became rough due to the grain ripening effect. With the increase in the soldering temperature to 430 °C, Cu3Sn no longer grew uniformly as observed during soldering at 310 °C, but exhibited various growth rates. Furthermore, some η-Cu6Sn5 transformed into η′-Cu6Sn5 during cooling, and the following orientation groups between η′-Cu6Sn5 and η-Cu6Sn5, i.e., {102}η′ and {<math>112‾0</math>}η, {112}η′ and {<math>101‾0</math>}η, and {<math>2‾01</math>}η′ and {0001}η, were found to be near-parallel. The Cu3Sn grains were preferably oriented with [203] and [100] crystal orientations parallel to transverse direction (TD) at both temperatures. Noteworthy, the Cu3Sn grains with [203]//TD and [010]//ND grew much faster than those with other orientations at 430 °C. Moreover, molecular dynamics simulation showed that the diffusion coefficients of atoms in Cu3Sn crystals along [203] direction were significantly greater than those in other low-index crystal directions. After soldering, two types of full Cu3Sn joints obtained at different temperatures exhibited different shear strength and fracture mechanisms.

Three-dimensional Placement Rules of Cu6Sn5 Textures Formed on the (111)cu and (001)cu Surfaces Using Electron Backscattered Diffraction

Formation and evolution of irregularly arranged prism-type Cu6Sn5 grains on electroplated (111) textured Cu

Thermal and Compositional Fields to Maneuver Cu 6 Sn 5 Intermetallic Growth on (111) Nanotwinned Copper Substrate

Influence of Cu Orientation on the Growth of Cu-Sn Intermetallics and Interfacial Reaction of Cu/Sn Diffusion Couple

Formation Mechanism and Orientation of Cu3Sn Grains in Cu–Sn Intermetallic Compound Joints

The Effect of Cu Orientation on Fracture Location in Cu<inf>3</inf>Sn-Cu Interface Structure Under Monotonic Loading Condition by Molecular Dynamics Simulation

Relationship between morphologies and orientations of Cu6Sn 5 grains in Sn3.0Ag0.5Cu solder joints on different Cu pads

The Effect of Pressure and Orientation on Cu-Cu3Sn Interface Reliability under Isothermal Ageing and Monotonic Traction Via Molecular Dynamics Investigation

Influence behavior and mechanism of crystal orientation of Cu 6 Sn 5 coating on interfacial intermetallic compounds growth in Sn-0.7Cu/Cu solder joint

Study on Cu6Sn5 Morphology and Grain Orientation Transition at the Interface of (111) Nt-Cu and Liquid Sn

The Effect Of Cu Orientation On Fracture Location In Cu3sn-Cu Interface Structure Under Monotonic Loading Condition By Molecular Dynamics Simulation

Influence of texture of Cu on the growth of Cu-Sn intermetallic compounds

Growth mechanism of Cu-Sn full IMC joints on polycrystalline and single crystal Cu substrate

A Molecular Dynamics Investigation of the Effect of Pressure and Orientation on the Cu Consumption in Cu-Cu3Sn Interface under Isothermal Ageing and Its Dissipative Mechanisms during Traction

Study on morphology and interface relationship between Ag3(Sn, In) and Cu6(Sn, In)5

Nucleation and growth of Cu6Sn5 during the aging process of Cu/Sn interface in electronic packaging-by in-situ TEM

Experimental and computational investigation of low temperature Cu-Sn solid-state-diffusion bonding for 3D integration

Influence Of Soldering Temperature And Dwelling Time On Morphological Evolution Of Cu6sn5 Intermetallic Compound At The Sn-3.0ag-0.5cu/Cu Interface

Morphologies and grain orientations of CuSn intermetallic compounds in Sn3.0Ag0.5Cu/Cu solder joints

Morphology evolution and grain orientations of intermetallic compounds during the formation of full Cu3Sn joint

Analysis of Cu6sn5 Grain Orientations in Sn3.0ag0.5cu Lead-Free Solder Joints