Abstract:Yttrium oxide doped with europium has a great prospective for FED and PDP phosphor application. In present study, the precursor of yttrium oxide hydroxide nitrate nanorod, which was prepared via hydrothermal reaction route using PEG-6000 as template from the starting Y(NO3)(3) and KOH reactant system, was used to prepare Y2O3:Eu3+ nanorod via a post annealing process during which the precursor with adjustable shape and size was transformed to final Y2O3:Eu3+ product. XRD, field emission scanning electron microscopy (FE-SEM) and photoluminescence spectra (PL) were used to characterize the crystalline, morphology and luminescence properties of as-formed Y2O3:Eu3+ products synthesized at different post annealing temperatures, respectively. The results indicate that grain morphology of obtained Y2O3:Eu3+ product was nanorod with a mean diameter of about 40 similar to 60 nm and length of about 500 similar to 700 nm, the nanorod structure and morphology of obtained Y2O3:Eu3+ product maintained during post annealing process and the size varied slightly with different annealing temperatures. Pure cubic Y2O3:Eu3+ phase was formed and the size was the smallest at annealing treatment of 500 degrees C. Under the annealing temperature below 500 degrees C its diameter increased with increasing annealing temperature, and remained in a stable size when the annealing temperature was above 500 degrees C. The PL spectra of excitation spectra of Y2O3:Eu3+ product show that it exhibits excitation band located at about 395 and 468 nm, respectively. Above two excitation bands could be ascribed to the transition 4f-4f of Eu3+ ions in the Y2O3 host. On the other hand, the main emission peaks of the as-prepared products could be ascribed to the Eu3+ ions transition from D-5(0) to F-7(2). Furthermore, the luminescent intensity was improved about three times when the annealing temperature increased from 500 to 1000 degrees C.

Facile Preparation and Fluorescence Enhancement of Mesoporous Eu-doped-Y 2 O 3 Phosphors

Synthesis of Y2O3:Eu3+ phosphors by surface diffusion and their photoluminescence properties

Synthesis and photoluminescence of nano-Y2O3:Eu3+ phosphors

Solution Combustion Synthesis and Enhanced Luminescence of Eu3+-activated Y2Ce2O7 Phosphor Nanopowders

Photoluminescence Properties of Y2SiO5 Doped with Eu3+ Phosphor

Facile solvothermal synthesis of gear-shaped submicrostructured Y 2O 3:Eu 3+ phosphor

Preparation, Characterization, and Optical Properties of Nano- and Submicron-Sized Y2o3:Eu3+ Phosphors

Synthesis and luminescence properties of Y 2O 3:Eu with flower-like microstructure

Microstructure and Photoluminescent Properties of Y2o3:Eu3+ Phosphors Synthesised by Precipitation and Combustion Methods

Synthesis and Iuminescent Properties of Y2O3 :Eu3+ Red Phosphor

Facile synthesis and luminescence properties of uniform and well-dispersed YF 3:Eu 3+ architectures

Synthesis and Luminescence Properties of Ypo4:Eu3+ Nanophosphor

Preparation and red long-afterglow luminescence of Y2O3: Eu, Dy

Preparation And Luminescence Properties Of Y2o3 : Eu3+ Nanorods Via Post Annealing Process

Patterning And Luminescent Properties Of Nanocrystalliney(2)O(3): Eu3+ Phosphor Films By Sol-Gel Soft Lithography

Synthesis of Y3al5o12 : Eu3+ Phosphor by Sol-Gel Method and Its Luminescence Behavior

Controllable preparation and fluorescence property of spherical nano-phosphor YPO4:Eu3+

Luminescent Properties of Y2O3:Eu Synthesized by Sol–gel Processing

Synthesis of Eu3+ doped yttrium orthosilicate phosphor by sol-combustion method

Morphology-tailored Synthesis and Luminescent Properties of Y 2 O 3 :Eu 3+ Phosphors

Controlled Hydrothermal Synthesis and Luminescent Properties of Y2WO6:Eu3+ Nanophosphors for Light-Emitting Diodes