Abstract:Yttrium oxide doped with europium has a great prospective for FED and PDP phosphor application. In present study, the precursor of yttrium oxide hydroxide nitrate nanorod, which was prepared via hydrothermal reaction route using PEG-6000 as template from the starting Y(NO3)(3) and KOH reactant system, was used to prepare Y2O3:Eu3+ nanorod via a post annealing process during which the precursor with adjustable shape and size was transformed to final Y2O3:Eu3+ product. XRD, field emission scanning electron microscopy (FE-SEM) and photoluminescence spectra (PL) were used to characterize the crystalline, morphology and luminescence properties of as-formed Y2O3:Eu3+ products synthesized at different post annealing temperatures, respectively. The results indicate that grain morphology of obtained Y2O3:Eu3+ product was nanorod with a mean diameter of about 40 similar to 60 nm and length of about 500 similar to 700 nm, the nanorod structure and morphology of obtained Y2O3:Eu3+ product maintained during post annealing process and the size varied slightly with different annealing temperatures. Pure cubic Y2O3:Eu3+ phase was formed and the size was the smallest at annealing treatment of 500 degrees C. Under the annealing temperature below 500 degrees C its diameter increased with increasing annealing temperature, and remained in a stable size when the annealing temperature was above 500 degrees C. The PL spectra of excitation spectra of Y2O3:Eu3+ product show that it exhibits excitation band located at about 395 and 468 nm, respectively. Above two excitation bands could be ascribed to the transition 4f-4f of Eu3+ ions in the Y2O3 host. On the other hand, the main emission peaks of the as-prepared products could be ascribed to the Eu3+ ions transition from D-5(0) to F-7(2). Furthermore, the luminescent intensity was improved about three times when the annealing temperature increased from 500 to 1000 degrees C.

Synthesis and Luminescence Properties of Ypo4:Eu3+ Nanophosphor

Luminescence Properties of Yb2+ Doped NaBaPO4 Phosphate Crystals

Hydrothermal Method Synthesis and Characterization of Yvo4:Eu3+@Ypo4 Core-Shell Phosphor

Optical properties, energy transfer and thermal stability of spherical nano-phosphor YPO4:Eu3+:Sm3+

Hydrothermal synthesis and tunable luminescence of YPO4:Eu2+/Eu3+, Tb3+ nanocrystals

Hydrothermal Synthesis And Photoluminescence Of Eu2-Xsmxsn2o7 (X=0-2.0) Nanophosphors

Synthesis Process and Luminescence Properties of Ln3+ Doped NaY(WO4)2 Nanoparticles

Preparation And Luminescence Properties Of Y2o3 : Eu3+ Nanorods Via Post Annealing Process

Hydrothermal synthesis, microstructure and luminescence properties of BiPO4:Eu3+ phosphor

Synthesis and Spectra Properties of YVO<SUB>4</SUB>:Eu Nanoparticles: Synthesis and Spectra Properties of YVO<SUB>4</SUB>:Eu Nanoparticles

Controlled Synthesis of Ln(3+) (ln = Tb, Eu, Dy) and V5+ Ion-Doped Ypo4 Nano-/Microstructures with Tunable Luminescent Colors

Synthesis and Properties of Europium-Based Phosphors on the Nanometer Scale: Eu2O3, Gd2O3:Eu, and Y2O3:Eu.

SYNTHESIS OF Y_2O_3∶Eu NANOCRYSTALLINE BY COMPLEX PRECURSORS

Synthesis of Nanometer Y2o3 : Eu Phosphor and Its Luminescence Property

Facile synthesis of monodisperse LuPO4:Eu3+/Tb3+ hollow nanospheres and their luminescence properties

Luminescent Properties of Li+ Doped Nanosized Y2O3:Eu

Rare earth activated nanosized oxide phosphors: synthesis and optical properties

Roles of (NH4)2HPO4 and NH4H2PO4 in the phase transition and luminescence enhancement of YPO4:Eu

Luminescent properties and energy transfer mechanism from Tb3+ to Eu3+ in color adjustable nano Ca5(PO4)3(OH): Eu3+,Tb3+ phosphors

Synthesis and Luminescence Properties of New Red-Emitting Phosphors YGe0.5M0.5O4:Eu3+ (m=mo, W)

Synthesis, Characterization and Luminescent Properties of Needle-Like Lanthanide-Doped Orthorhombic Y5O4F7