Hydrothermal Synthesis and Photoluminescent Properties of Li2Sr0.996SiO4:Pr3+0.004 Phosphors for White-Led Lightings

Zhou Xiaojun,Xiong Zhaoxian,Xue Hao,Lin Yisen,Song Chunxiao

DOI: https://doi.org/10.1016/s1002-0721(14)60410-5

IF: 4.632

2015-01-01

Journal of Rare Earths

Abstract:Red phosphors, Li2Sr0.996SiO4: Pr3+0.004, with different hydrothermal conditions were prepared via hydrothermal synthesis and then heat-treatment. The chemical structures of the phosphors were identified with X-ray diffraction (XRD). Surface morphological features were observed by scanning electron microscopic (SEM) investigation. Spectra of excitation and emission for the phosphors were also obtained by a spectrophotometer. Results showed that the optimum conditions were as follows: pH value of solution was 1−2, reaction temperature was at 180 °C for 24 h. The as-prepared phosphors exhibited two excitation dominant peaks at 451 and 486 nm, attributed to transitions of 3H4→3P2 and 3H4→3P0 of Pr3+, respectively. A narrow emission peak at 610 nm corresponded to the energy level transition of 3P0→3H6 of Pr3+ under excitation of light at 451 nm, which indicated promising candidate red phosphors for blue LED chips.