Abstract:The C=C double bonds in the main chain of hydroxyl-terminated polybutadiene (DHTPB), obtained by the degradation of polybutadiene rubber, were partially epoxided using m-chloroperoxybenzoic acid (mCPBA) as epoxidation reagent. A series of epoxided HTPBs (EHTPB) with different epoxy contents (5%, 10% and 15%) were prepared by tuning the molar ratio of mCPBA to C=C double bonds. The structures of EHTPBs were characterized by Fourier transform-infrared (FTIR), nuclear magnetic resonance (H-1-NMR) spectroscopy and gel permeation chromatography (GPC). The epoxy percent in EHTPBs from H-1-NMR spectra was in accordance with the design. In addition, a series of EHTPB-based polyurethane elastomers (EPU) were prepared by the reaction between EHTPB and 4,4'-diphenylmethane diisocyanate with 1,4-butanediol as a chain extender. Mechanical and thermal properties of the EPU samples were characterized by tensile test, differential scanning calorimetry (DSC) and thermal gravity analysis (TGA). With increased epoxy percent in EHTPB, the Young's modulus and the tensile strength of the EPU samples increased, whereas the elongation at break decreased. The sample EPU10 prepared with 10% of epoxy had the best mechanical properties with 8.82 MPa as Young's modulus, 7.83 MPa as tensile strength, and (485 +/- 23)% as elongation at break. The elasticity recovery of the EPU sample was slightly better than HTPB-based PU (EPU0). The results with TGA test showed that the thermal degradation of EPU, similar to EPU0, was divided into three stages. However, the EPU samples had better thermal stability with the initial degradation temperature at 210 degrees C, about 30 degrees C higher than that of EPU0. The DSC results showed that the glass transition temperature (T-g) of EPU gradually increased as epoxy percent was increased, though still lower than that of HTPB (FHTPB) based PUs prepared by free-radical polymerization.

Synthesis and Characterization of HALS/UV-absorbers Bifunctionalized Core-Shell Elastomer and Its Application in Polyoxymethylene

Preparation and Properties of Epoxided Hydroxyl-terminated Polybutadiene Based Polyurethane Elastomers

Preparation and Characterization of MMA-BA-DMAEMA Terpolymer Latex

Preparation and characterization of a high molecular weight UV-stabilizer based on a derivative of 2,4-dihydroxybenzophenone and its application in polymer materials

Preparation and Characterisation of Novel Cross-Linked Poly (IBOMA-BA-DFMA) Latex

Preparation of a Novel Stabilizer and Its Thermal‐oxidative Stabilization Effect on Polyamide 6

Synthesis of Multifunctional Core–shell Toughening Agent with Light Stability and Its Application in Polycarbonate

Synthesis and Application of Hydroxyethyl Methacrylate Modified Waterborne Polyurethane

Synthesis and characterization of hyperbranched polyurethane acrylates used as UV curable oligomers for coatings

Photopolymerization and toughening performance in polypropylene of hyperbranched polyurethane acrylate

Synthesis and Properties of Cationic Photopolymerizable Hyperbranched Polyesters with Terminal Oxetane Groups by the Couple-Monomer Polymerization of Carboxylic Anhydride with Hydroxyl Oxetane

Synthesis and properties of reactive polyurethane hot melt adhesive based on a novel phosphorus-nitrogen-containing polyol

Preparation and Characterization of Uv-Curable Hyperbranched Polyurethane Acrylate

Preparation of high-performance polyurethane-polyacrylate coatings based on hyperbranched structure and application in anti-ultraviolet film

Synthesis and characterization of crosslinked transparent poly(ester-urethane-acrylate) containing methyl methacrylate

A novel polymethyl methacrylate (PMMA) with excellent optical and thermal properties-bearing hydroxyadamamtyl substituent

The preparation and mechanism of permanently flame retardancy, antistatic, good toughness and high transparent poly(methyl methacrylate)

EFFECT OF COMPOSITIONS OF MONOMERS AND EMULSIFIERS ON PROPERTIES OF CORE-SHELL ACRYLATE EMULSION

Synthesis, Photopolymerization Kinetics, and Thermal Properties of Uv-Curable Waterborne Hyperbranched Polyurethane Acrylate Dispersions

Core-Shell Emulsion Copolymerization and Characterization of Polysiloxane Bearing Vinylic Function/Acrylate Monomer

Fluorinated Modification of Hyperbranched Polyesters Used for Improving the Surface Property of Uv Curing Coatings