Abstract:After the extraction of molybdenum from the spent HDS catalyst, a residue containing aluminum, nickel, cobalt, and a small amount of molybdenum was obtained. The simultaneous recovery of nickel, cobalt, aluminum, and residual molybdenum from molybdenum leach residue can be achieved through hydrochloric acid leaching. In the work presented herein, the extraction of molybdenum, cobalt, and nickel from the acidic leach solution of molybdenum leach residue was investigated. Trioctyl tertiary amine can selectively extract cobalt and molybdenum from the acidic leach solution, the extraction of both cobalt and molybdenum reached more than 99% after two-stage countercurrent extraction. The combination of pure water and 25% ammonia water can be utilised for the separation and extraction of cobalt and molybdenum from the loaded cobalt-molybdenum organic phase. After the extraction of cobalt and molybdenum, a synergistic extraction system comprising decyl 4-picolinate and dinonylnaphthalene sulfonic acid can be employed for nickel extraction, achieving a nickel extraction exceeding 99.70% while maintaining aluminum extraction at only 0.32% after undergoing four-stage countercurrent extraction. The nickel stripping efficiency can reach 99.50% after four-stage countercurrent stripping, using a stripping agent of 2 mol/L H 2 SO 4 . Après l'extraction du molybdène du catalyseur HDS usé, on a obtenu un résidu contenant de l'aluminium, du nickel, du cobalt et une petite quantité de molybdène. On peut obtenir la récupération simultanée du nickel, du cobalt, de l'aluminium et du molybdène résiduel à partir des résidus d'attaque du molybdène grâce a une lixiviation à l'acide chlorhydrique. Dans le travail présenté ici, on a examiné l'extraction du molybdène, du cobalt et du nickel de la solution d'attaque acide des résidus d'attaque du molybdène. L'amine de trioctyle tertiaire peut extraire sélectivement le cobalt et le molybdène de la solution d'attaque acide, l'extraction du cobalt et du molybdène atteignant plus de 99% après une extraction à contre-courant en deux étapes. On peut utiliser la combinaison d'eau pure et de 25% d'eau ammoniaquée pour la séparation et l'extraction du cobalt et du molybdène de la phase organique chargée de cobalt-molybdène. Après l'extraction du cobalt et du molybdène, on peut utiliser un système d'extraction synergique comprenant du picolinate-4 décyle et de l'acide sulfonique dinonylnaphthalène pour l'extraction de nickel, obtenant une extraction du nickel dépassant 99.70% tout en maintenant l'extraction de l'aluminium à seulement 0.32% après avoir subi une extraction à contre-courant en quatre étapes. L'efficacité de l'élimination du nickel peut atteindre 99.50% après l'élimination à contre-courant en quatre étapes, en utilisant un agent d'élimination de 2 mol/L H 2 SO 4 .

Alkali extraction of valuable metals from spent Mo–Ni/Al 2 O 3 catalyst

Cleaner recycling of spent Ni–Mo/γ-Al2O3 catalyst based on mineral phase reconstruction

Metals Leaching Mechanism of Fe or/and Mo Modified Raney-Ni Catalysts and Their Catalytic Hydrogenation of Glucose

Stepwise separation and recovery of molybdenum, vanadium, and nickel from spent hydrogenation catalyst

Recovery of nickel and molybdate from ammoniacal leach liquor of spent hydrodesulfurization catalyst using LIX84 extraction

Highly efficient recovery of molybdenum from spent catalyst by optimized process.

Extraction of Molybdenum from Spent HDS Catalyst by Pressure Alkaline Leaching

The Acute Chest in General Practice

Ultrasound-assisted Oil Removal of Γ-Al2o3-based Spent Hydrodesulfurization Catalyst and Microwave Roasting Recovery of Metal Mo.

Recovery and Regeneration of Al 2 O 3 with a High Specific Surface Area from Spent Hydrodesulfurization Catalyst CoMo/Al 2 O 3

Extraction, phase transformation and kinetics of valuable metals from nickel-chromium mixed metal oxidized ore

Reclamation Of Acid Pickling Waste: Preparation Of Nano Alpha-Fe2o3 And Its Catalytic Performance

Extraction of molybdenum, cobalt, and nickel from acidic leach solution of molybdenum leach residue of spent hydrodesulfurization catalyst

Negligible emissions and highly efficient recovery of Mo, V, and Al from spent hydroprocessing catalysts through alkaline leaching and solvent extraction

MAS NMR, TPR, and TEM Studies of the Interaction of NiMo with Alumina and Silica–alumina Supports

Economical and efficient recovery of Pd and Al2O3 from spent Pd/Al2O3 catalyst with integrated sodium roasting−reductive leaching process

Separation and Recovery of Vanadium, Nickel, and Aluminum from Acid Leaching Solution of Spent Hydrodesulfurization Catalyst by a Solvent Extraction-Oxalic Acid Precipitation Process

Recovering valuable metals from spent hydrodesulfurization catalyst via blank roasting and alkaline leaching

Enrichment of Ni–Mo–V via pyrometallurgical reduction from spent hydrogenation catalysts and the multi-reaction mechanism

Intensified bioleaching of spent Co-Mo catalyst by addition of extracellular polymeric substances (EPS) and its mechanisms exploration

Alkali fusion using sodium carbonate for extraction of vanadium and tungsten for the preparation of synthetic sodium titanate from spent SCR catalyst