Abstract:Spent petroleum hydroprocessing catalysts (HPCs) are considered hazardous waste due to their high content of heavy metals and organic pollutants , posing a risk of environmental pollution and significant loss of valuable metals if not properly disposed. This study aimed to characterize the spent HPCs using optical microscopy, SEM-EDS, XRF, C & S analyzer, XRD, and XPS. Additionally, the effectiveness of six organic solvents in removing the black oil covering the surface of spent HPCs was investigated. Furthermore, the recovery of Mo, V, and Al from the spent HPCs was examined through stepwise leaching using NaOH + NaClO 2 and NaOH, followed by the separation of Mo, V, and Al via selective precipitation of Al and solvent extraction using Aliquat 336. The results indicated that toluene and tetrahydrofuran exhibited the highest efficiency in removing the black oil. Under the optimized oxidizing alkaline leaching conditions (0.09 g/mL NaOH + 0.05 g/mL NaClO 2 , 90 °C, 1 h), Mo, V, and Al achieved leaching efficiencies of 99.9 %, 99.9 %, and 20.1 %, respectively. Subsequently, Al in the residue was recovered through leaching with NaOH, resulting in a total leaching efficiency of 95 % under the optimized alkaline leaching conditions (0.12 g/mL NaOH, 180 °C, 3 h). The Al in both leaching solutions was precipitated by adjusting the pH to 8.60. For the subsequent Mo/V separation, the best conditions involved either four stages of counter-current extraction or two stages of cross-current extraction using a solution of 21 wt% Aliquat 336 dissolved in a mixture of kerosene and isooctanol (volume ratio 9:1) at a pH of 8.60. Finally, a hydrometallurgical flowchart for the recovery of Mo, V, and Al from spent HPCs was proposed.

Economical and efficient recovery of Pd and Al2O3 from spent Pd/Al2O3 catalyst with integrated sodium roasting−reductive leaching process

Recovery Of Palladium And Aluminum From Spent Catalysts By Roasting-Leaching

Recovery Of Palladium From Spent Pd/Al2o3 Catalyst By Hydrochloric Acid Leaching

A Novel Process for Comprehensive Utilization of Spent Al_2O_3-based Catalyst

Efficient Recovery of All Valuable Metals from Spent HDS Catalysts: Based on Roasting Mechanisms for Enhanced Selective Leaching and Separation

Study on the Recycling of Valuable Metals in Spent Al2O3-based Catalyst

New Technique of Comprehensive Utilization of Spent Al 2 O 3 -Based Catalyst

Recovering valuable metals from spent hydrodesulfurization catalyst via blank roasting and alkaline leaching

Efficient and Selective Recovery of Mo and V from Spent Hydrodesulfurization Catalysts Via Oxidation Roasting Followed by Na2CO3 and NaOH Leaching

Research on Recovery of Palladium From Spent Catalyst

Cleaner recycling of spent Ni–Mo/γ-Al2O3 catalyst based on mineral phase reconstruction

Recovering Palladium from Chloridizing Leaching Solution of Spent Pd/Al<Subscript>2</Subscript>O<Subscript>3</Subscript> Catalyst by Sulfide Precipitation

New Technology for Pd Recovery from Selectively Leached Residue of Waste Palladium Catalyst

Negligible emissions and highly efficient recovery of Mo, V, and Al from spent hydroprocessing catalysts through alkaline leaching and solvent extraction

Recovery and Regeneration of Al 2 O 3 with a High Specific Surface Area from Spent Hydrodesulfurization Catalyst CoMo/Al 2 O 3

Alkali extraction of valuable metals from spent Mo–Ni/Al 2 O 3 catalyst

Efficient enrichment of platinum group metals from spent automotive catalysts by alkaline hydrothermal treatment and the subsequent acid leaching method

Recovery of Aluminum from Molybdenum Extraction Residue of Spent Hydrodesulfurization Catalyst

Recovery of Mo and Ni from spent acrylonitrile catalysts using an oxidation leaching–chemical precipitation technique

A Promising Approach to Recover a Spent SCR Catalyst: Deactivation by Arsenic and Alkaline Metals and Catalyst Regeneration

Ultrasound-assisted Oil Removal of Γ-Al2o3-based Spent Hydrodesulfurization Catalyst and Microwave Roasting Recovery of Metal Mo.