Abstract:A Ni/scandia-stabilized zirconia (ScSZ) cermet anode was modified by coating with nano-sized gadolinium-doped ceria (GDC, Gd0.2Ce0.8O2) prepared using a simple combustion process within the pores of the anode for a solid oxide fuel cell (SOFC) running on methane fuel. X-ray diffraction (XRD) and scanning electron microscopy (SEM) were employed in the anode characterizations. Then, the short-term stability for the cells with the Ni/ScSZ and 2.0wt.%GDC-coated Ni/ScSZ anodes in 97%CH4/3%H2O at 700°C was checked over a relative long period of operation. Open circuit voltages (OCVs) increased from 1.098 to 1.179V, and power densities increased from 224 to 848mWcm−2, as the operating temperature of an SOFC with 2.0wt.%GDC-coated Ni/ScSZ anode was increased from 700 to 850°C in humidified methane. The coating of nano-sized Gd0.2Ce0.8O2 particle within the pores of the porous Ni/ScSZ anode significantly improved the performance of anode supported cells. Electrochemical impedance spectra (EIS) illustrated that the cell with Ni/ScSZ anode exhibited far greater impedances than the cell with 2.0wt.%GDC-coated Ni/ScSZ anode. Introduction of nano-sized GDC particles into the pores of porous Ni/ScSZ anode will result in a substantial increase in the ionic conductivity of the anode and increase the triple phase boundary region expanding the number of sites available for electrochemical activity. No significant degradation in performance has been observed after 84h of cell testing when 2.0wt.%GDC-coated Ni/ScSZ anode was exposed to 97%CH4/3%H2O at 700°C. Very little carbon was detected on the anodes, suggesting that carbon deposition was limited during cell operation. Consequently, the GDC coating on the pores of anode made it possible to have good stability for long-term operation due to low carbon deposition.

Reaction Process in the Ni-SDC Cermet Anode

Effect of Ceria Components on Anode Performance of Ni-base Anode in Hydrocarbon Fueled SOFC

Reaction Process in the Ni–ScSZ Anode for Hydrocarbon Fueled SOFCs

H2 Oxidation Pathways on Ni-ceria Surface by Electrical Conductivity Relaxation Method

Ni-Sm2o3 Cermet Anodes for Intermediate-Temperature Solid Oxide Fuel Cells with Stabilized Zirconia Electrolytes

Effect Of Samaria Doped Ceria Impregnation On The Electrochemical Performance Of Strontium Doped Lanthanum Chromium Manganite Anode For Solid Oxide Fuel Cells

In situ transmission electron microscopic observations of redox cycling of a Ni-ScSZ cermet fuel cell anode

H 2 and CO Oxidation Process at the Three-Phase Boundary of Cu-ceria Cermet Anode for Solid Oxide Fuel Cell

Synthesis and Properties of Ni–SDC Cermets for IT–SOFC Anode by Co-Precipitation

A Novel Method to Purposely Modify the Anode/Electrolyte Interface in Solid Oxide Fuel Cells

Performance of Ni/Scsz Cermet Anode Modified by Coating with Gd0.2ce0.8o2 for an Sofc Running on Methane Fuel

Evaluation of Ni and Ni–Ce0.8Sm0.2O2−δ (SDC) Impregnated 430L Anodes for Metal-Supported Solid Oxide Fuel Cells

Stability of Ni Base Anode for Direct Hydrocarbon SOFCs

Redox of Ni/YSZ Anodes and Oscillatory Behavior in Single-Chamber SOFC under Methane Oxidation Conditions

Materials and Reaction Mechanisms at Anode/Electrolyte Interfaces for SOFCs

Performance and Sulfur Poisoning of Ni/CeO2 Impregnated La0.75Sr0.25Cr0.5Mn0.5O3−δ Anode in Solid Oxide Fuel Cells

Preparation and Performance of Ni-CU/SDC Anodes

Preparation and Performance Test of Ni-Fe/SDC Cell Anode

Mechanism and Kinetics of Ni-Y2O3-ZrO2Hydrogen Electrode for Water Electrolysis Reactions in Solid Oxide Electrolysis Cells

Atomic scale understanding of the role of Ni/XSZ interface in internal reforming SOFC in low CH 4 /H 2 O environment

Imaging of CH4 Decomposition Around the Ni/YSZ Interfaces under Anodic Polarization