Abstract:The unique properties of Nb2O5 as a solid acid have led to catalytic applications in various reactions catalyzed by acids. The surface acidity and stability of Nb2O5 can be enhanced by the addition of phosphate ions. In this work, amorphous Nb2O5 and NbOPO4 samples were synthesized. The interactions of ammonia, methanol, water and dimethyl ether with Nb2O5 and NbOPO4 were investigated by means of adsorption microcalorimetry, adsorption infrared spectroscopy (FT-IR) and temperature-programmed desorption (TPD) techniques. The results of microcalorimetry and FT-IR for NH3 adsorption have shown that NbOPO4 is much more acidic than Nb2O5 due to its higher surface area, and that both Brønsted and Lewis acid sites are present on the surface of Nb2O5 and NbOPO4. Water adsorption microcalorimetry results indicate that a small amount of water was strongly chemisorbed on Nb2O5 and NbOPO4 while most of the adsorbed water corresponded to physical adsorption. The results of methanol adsorption microcalorimetry, methanol adsorption FT-IR and methanol TPD suggest that methanol is mainly strongly dissociatively adsorbed on Nb2O5 and NbOPO4 to form methoxy species and DME could be produced from the dehydration of methoxy species. DME adsorption microcalorimetry and FT-IR showed that DME was mainly molecularly chemically adsorbed on Nb2O5 and NbOPO4, while a small amount of DME was dissociatively adsorbed. The probe molecules (NH3, methanol, H2O and DME) used in this work were adsorbed more strongly on NbOPO4 than on Nb2O5 because of the stronger acidity of NbOPO4. In the reaction of methanol dehydration, although Nb2O5 and NbOPO4 were not as active as a H-ZSM-5 zeolite, they exhibited 100% selectivity to the DME product and a good stability of the activity in the temperature range relevant to the reaction (453–573K), without coke formation.

(Al1−xcrx)4b6o15 (0.08≤x≤0.14): Metal Borates Catalyze the Dehydration of Methanol into Dimethyl Ether

Systematic Study of Cr3+ Substitution into Octahedra-Based Microporous Aluminoborates.

Highly Dispersed CrOx Nanoparticle-Modified NaZSM-5 for Dehydration of Methanol to Dimethyl Ether

Highly Dispersed Crox Nanoparticles Modified Nazsm-5 for Lower Temperature Dehydration of Methanol to Dimethyl Ether

Influence of Acid-Base Properties of ZnMgAl-mixed Oxides for the Synthesis of 1-Methoxy-2-propanol

Dehydration of Methanol to Dimethyl Ether over Nb2O5 and NbOPO4 Catalysts: Microcalorimetric and FT-IR Studies

Facile Synthesis of Ptcu3 Alloy Hexapods and Hollow Nanoframes As Highly Active Electrocatalysts for Methanol Oxidation

Understanding how the crystalline nature of Fe-promoted alumino-borate PKU-1 catalyst affects Glycerin ketalization: the systematic control of surface composition and acidity

An atom-economic reaction for synthesis of 1-phenoxy-2-propanol over Al2O3/MgO

Aluminum Hydroxide Secondary Building Units in a Metal–Organic Framework Support Earth-Abundant Metal Catalysts for Broad-Scope Organic Transformations

Synthesis, Characterization, and Catalytic Performance of Cr-Incorporated Aluminoborate Octahedral Molecular Sieves

Fe doped aluminoborate PKU-1 catalysts for the ketalization of glycerol to solketal: Unveiling the effects of iron composition and boron

The synthesis of endurable B–Al–ZSM-5 catalysts with tunable acidity for methanol to propylene reaction

The Dehydration of Methanol to Dimethyl Ether over a Novel Solid Acid-base Catalyst

Microporous Aluminoborates with Large Channels: Structural and Catalytic Properties

Preparation and Characterization of Cu-Cr-M-O Catalyst for Synthesis of Methanol and Methyl Formate at Low Temperature in Slurry Phase

Adsorption and Dehydration of Methanol on Al2o3 Catalyst

PKU-3: an HCl-Inclusive Aluminoborate for Strecker Reaction Solved by Combining RED and PXRD

Surface acidity and the dehydration of methanol to dimethyl ether

PKU-5: an Aluminoborate with Novel Octahedral Framework Topology.

Reaction Kinetics of Methanol Dehydration over Combined AI203-HZSM-5 Solid Acids