Abstract:CaCu3Ti4O12 (CCTO) ceramics with smaller grain size usually show a low dielectric constant by using the conventional sintering method. In this work, the pure CCTO ceramics with smaller grain size prepared by the spark plasma sintering method (SPS) present the giant dielectric constant (ε′) over a wide temperature range. The dense CCTO ceramics have been rapidly fabricated by a sol–gel process and the SPS method at different sintering temperatures. The XRD patterns indicate a single CCTO phase with cubic perovskite structure in SPS-CCTO ceramics. The SEM images demonstrate that the average grain size of the SPS-CCTO ceramics increases from about 2.23(± 1.56) μm to 4.68(± 2.45) μm with the increases of the SPS sintering temperature from 800 to 900 °C. The obvious electrically heterogeneous characteristics in these SPS-CCTO ceramics are affirmed by the complex impedance spectroscopy analysis. The highest dielectric constant of 1.58 × 104 at 103 Hz is found in SPS-CCTO3 (900 °C) ceramics, and the temperature coefficients of the dielectric constant Δε′ in SPS-CCTO1 (800 °C) and SPS-CCTO2 (850 °C) ceramics with the high ε′ values are less than ± 15% (Δε′ < ±15%) over a temperature range of − 30 to 80 °C; the high dielectric constant is due to the phenomenon of Rg ≪ Rgb based on the internal barrier layer capacitance (IBLC) effect. The larger nonlinear coefficient of 9.07, as well as the enhanced breakdown field of 3257 V/cm are achieved in SPS-CCTO1 ceramics, which is attributed to the increased grain boundary resistance and the Schottky barrier at grain boundary regions. These results indicate that the SPS method is an effective way to control the grain size and improve the electrical properties of the CCTO ceramics for energy storage application.

Microwave-Assisted Synthesis of High Dielectric Constant CaCu 3 Ti 4 O 12 from Sol–Gel Precursor

Preparation and characterization of CaCu 3 Ti 4 O 12 powders by non-hydrolytic sol–gel method

Preparation and characterization of CaCu3Ti4O12 powders by non-hydrolytic sol–gel method

Dielectric Properties and IV Characteristic of CaCu_3Ti_4O_(12)-MgTiO_3 Composite Ceramic Synthesized by Sol-Gel Method

Grain Size Effect on the Dielectric and Non-Ohmic Properties of CaCu3Ti4O12 Ceramics Prepared by the Sol-Gel Process

Rapid Fabrication and Improved Electrical Properties of CaCu3Ti4O12 Ceramics by Sol–gel and Spark Plasma Sintering Techniques

Structure, Properties, and Impedance Spectroscopy of CaCu3Ti4O12 Ceramics Prepared by Sol-Gel Process: Structure, Properties, and Impedance Spectroscopy of CaCu3Ti4O12

Low -temperature sintering of Al2O3 microwave dielectric ceramic doped with CuO-TiO2 gel

Synthesis and Characterization of CaTiO 3 -(Sm,nd)alo 3 Microwave Ceramics Via Sol–gel Method

Preparation and Dielectric Properties of (ca0.61,nd0.26)tio3 Nanoparticles by a Sol–gel Method

CaCu3Ti4O12 Ceramics from Basic Co-Precipitation (BCP) Method: Fabrication and Properties

Structure, Properties, And Impedance Spectroscopy Of Cacu3ti4o12 Ceramics Prepared By Sol-Gel Process

Effect of Europium Addition on the Microstructure and Dielectric Properties of CCTO Ceramic Prepared Using Conventional and Microwave Sintering

Calcining Temperature Dependence on Structure and Dielectric Properties of CaCu 3 Ti 4 O 12 Ceramics

Electrical Conduction and Dielectric Properties of the CaCu_3Ti_4O_(12) Ceramics Synthesized by SPS

Oleic Acid Assisted Synthesis of CaCu3Ti4O12 Powders and Ceramics by Sol–gel Process

Microstructure and Dielectric Properties of CaCu3Ti4O12 Ceramics by Quenching after Sintering in Low Vacuum and Thermobaric Treatment at 9 GPa

Enhanced Extrinsic Dielectric Response of TiO2 Modified CaCu3Ti4O12 Ceramics

Effect of Al substitution and secondary CuO phase on dielectric response in microwave-processed CaCu3Ti4−xAlxO12 ceramics

GIANT DIELECTRIC CONSTANT MATERIAL CaCu3Ti4O12 PREPARED BY SOL-GEL METHOD

Preparation of Tio2-Enriched Cacu3mn0.1ti3.9o12 Ceramics and Their Dielectric Properties