Abstract:Freezing-thawing (F-T) cycle is one of the main reason of concrete damage in cold regions. F-T cycle mainly lead to degradation of macroscopic mechanical properties of concrete by changing the number of micropores, mesopores and macropores, and causing severely damage to its internal texture. The variations of the physical and mechanical properties of concrete sample with different inclination angle of internal flaw exposed to different F-T cycles (0, 10, 30 and 50 cycles) under unconfined compression condition was deeply investigated based on the acoustic emission (AE) and nuclear magnetic resonance (NMR) technology. The evolution of the internal cracks are tracked in real-time by AE monitoring systems during the entire test process. Meanwhile, the micro-structure of the concrete sample after F-T cycle treatment is microscopically observed with T2 distribution by low-field nuclear magnetic resonance. The results show that the peak strength of concrete decreases with the increasing F-T cycles and increases as the increasing inclination angle of prefabricated flaw. The elastic modulus decreased gradually with the increase of F-T cycles. The elastic modulus of the sample without F-T cycles treatment increases with the increase of inclination angle of prefabricated flaw. As the flaw inclination angle increases from 0° to 90°, the F-T cycles increases from 0 to 50, the peak strain shows an obvious discreteness without monotone change. When the number of F-T cycle reaches 50, concrete blocks fall off from the sample surface. A continuum damage model considering F-T damage from different pore size is finally introduced to describe the damage evolution of concrete during compression test. The research results can be used to quantitatively evaluate the strength of concrete samples treated by F-T cycle without mechanical tests.

Probabilistic damage modeling and service-life prediction of concrete under freeze–thaw action

Development of Internal Moisture Transfer and Cumulative Residual Strain in Concrete under Freeze-Thaw Cycles

Cohesive Fracture and Probabilistic Damage Analysis of Freezing–thawing Degradation of Concrete

A stochastic damage model for evaluating the internal deterioration of concrete due to freeze–thaw action

Mesoscale Simulation of Fatigue Behavior of Concrete Materials Damaged by Freeze-Thaw Cycles

Stress Analysis for Concrete Materials under Multiple Freeze-Thaw Cycles

Environmental Factors Influencing The Durability Of Concrete Structures In Frost Environments

Structural behaviors evaluation of RC beam under frost damage - A methodology with meso-macro material/bond simulation and integrating into structural analysis

Flexural behaviour of reinforced concrete members subjected to freeze-thaw cycles

Reliability models and service life estimation of concrete structure under freeze-thaw action

Experimental Study on Mechanical Properties and Pore Structure Deterioration of Concrete under Freeze–Thaw Cycles

Predicting Method of Concrete Service Life Based on Damage Development Equation

Evaluation Method for the Service Life of Concrete under the Freeze-Thaw Action

Two‐dimensional Rigid Body Spring Method Based Micro‐mesoscale Study of Mechanical Strengthening/damaging Effects to Concrete by Frost Action

Dynamic Mechanical Properties and Visco-Elastic Damage Constitutive Model of Freeze–Thawed Concrete

RBSM based analysis on mechanical degradation of non-air entrained concrete under frost action – A general prediction with various water cement ratio, lowest temperatures and FTC numbers

Stress-strain relationship of concrete in freeze-thaw environment

Service Life Prediction of Recycled Concrete Based on Freezing-thawing Damage Parabola Model

Study on Freezing-Thawing damage mechanism and evolution model of concrete

Analysis on Reliability of Concrete under Freezing-Thawing Action and Evaluation of Residual Life

SERVICE LIFE PREDICTION OF ULTRA-HIGH PERFORMANCE CONCRETE UNDER FREEZE-THAW ENVIRONMENT