Process Intensification of the Synthesis of Poly(vinyl butyral) Using a Microstructured Chemical System

XY Lin,K Wang,JS Zhang,GS Luo

DOI: https://doi.org/10.1021/acs.iecr.5b00911

2015-01-01

Industrial & Engineering Chemistry Research

Abstract:In this work, we established a novel microstructured chemical system to intensify the synthesis process of poly(vinyl butyral) (PVB) based on the mixing enhancement principle of poly(vinyl alcohol) (PVA)-n-butanal aqueous solution with hydrochloric acid. Because of the high mixing performance, a higher temperature (30-60 degrees C) with much higher reaction rate was applied. Through a study of the parameters of flow rate, temperature, and feeding ratios of n-butanal and H+ to the hydroxyl groups in PVA, the apparent butyral group content in PVB reached more than 60% with a residence time of 1 min in a microreactor, and reached 75% with an additional hour of aging time, much shorter than the conventional 8-10 h in low temperature batch reactors. The size of the primary PVB particle was smaller than 10 mu m, which might reduce the time and water consumption in the post washing process. This work provides a good example for operating reactions between macromolecules and small molecules in a microreactor system.