Abstract:The microstructure of peritectic alloys of important applications determines the final properties of them. The growth of peritectic β phase which greatly influences the structure of peritectic systems is divided into three different types: peritectic reaction at TP: L + α → β, then solid-state peritectic transformation α → β and direct precipitation L → β. In addition to transparent organic systems, peritectic transformation was always analyzed using interrupted directional solidification during which the sample is kept stationary after experiencing a distance of directional growth. Then, the growth of β phase through peritectic transformation is accompanied with the migration of the α/β interface towards α phase below TP. However, it is found in SnNi peritectic system (L + Ni3Sn2 → Ni3Sn4) that the migration rate of Ni3Sn2/Ni3Sn4 interface is much larger than that of peritectic transformation. Further examination shows that this interface migration can also be induced by the diffusion-controlled liquid migration initiating at the Ni3Sn2/Ni3Sn4 interface. Based on the model describing the liquid migration process, the migration of the Ni3Sn2/Ni3Sn4 interface through liquid migration is predicted, which matches well with the experimental measurement. This shows that the diffusion-controlled liquid migration is dominant during the growth of β phase. Thus, the application of interrupted directional solidification should be further examined.

Microsegregation of Peritectic Systems in a Temperature Gradient: Analysis in Directionally Solidified Sn–36at.%Ni Peritectic Alloy

Local Melting/solidification During Peritectic Solidification in a Steep Temperature Gradient: Analysis of a Directionally Solidified Al–25at%Ni

The Diffusion-Controlled Remelting/resolidification Process in Directionally Solidified Sn-Mn Peritectic Alloy

On Melt Concentration at the Solid/liquid Interface During Preparation of Directionally Solidified Sn–36 At.%ni Peritectic Alloy

Non-equilibrium solidification of bulk undercooled Ni–P eutectic alloys

An Analysis of Non-Equilibrium Peritectic Reaction Driven by Solute Diffusion under a Temperature Gradient

Migration of Liquid Phase from the Primary/peritectic Interface in a Temperature Gradient

Dendrite Coarsening in Directionally Solidified Sn–36 At.%ni Peritectic Alloy in the Presence of the Migration of Secondary Dendrite Arms

On Migration of Primary/Peritectic Interface During Interrupted Directional Solidification of Sn-Ni Peritectic Alloy

Secondary Dendrite Arm Migration Caused by Temperature Gradient Zone Melting in the Directionally Solidified Sn–40 At.% Mn Peritectic Alloy

Microstructure and Microsegregation in A Ni-Based Single Crystal Superalloy Directionally Solidified under High Thermal Gradient

Influence of Solutal Convection on Solute Distribution of Melt During Preparation of Directionally Solidified Sn–36 At.%ni Peritectic Alloy

Convection Effects and Banding Structure Formation Mechanism During Directional Solidification of Peritectic Alloys Ii. Theoretical Analysis

Peritectic Reaction and Its Influences on the Microstructures Evolution During Directional Solidification of Fe–Ni Alloys

Liquid migration and peritectic transformation: Investigation on their contributions to growth of peritectic phase in interrupted directional solidification

Macrosegregation and channel segregation formation of faceted mushy zone in solidification of Sn–Ni hypereutectic alloy in a temperature gradient

Secondary Dendrite Arm Migration Caused by Temperature Gradient Zone Melting During Peritectic Solidification

Thermosolutal convection-induced freckle formation in steady and unsteady directional solidification: Analysis in Sn-Ni peritectic alloy

Investigation of the Non-Equilibrium Solidification and Microstructures of Al-Y Peritectic Alloys

Phase and Microstructure Selection in Directionally Solidified Peritectic Alloys with Convection

Peritectic Transformation and Primary Α-Dendrite Dissolution in Directionally Solidified Pb–26%Bi Alloy