Reaction of NO + CO over Ce-Modified Cu–FeOx Catalysts at Low Temperature
Luyuan Wang,Xingxing Cheng,Zhiqiang Wang,Rongfeng Sun,Gaiju Zhao,Tai Feng,Chunyuan Ma
DOI: https://doi.org/10.1021/acs.energyfuels.9b02839
IF: 4.6541
2019-01-01
Energy & Fuels
Abstract:A series of Ce-modified Cu-FeOx catalysts were synthesized with a sol-gel hydrothermal method. These catalysts contained different molar ratios of Ce, Cu, and Fe, and were applied to the process of NO catalytic removal by CO (CO-deNO). The physical and chemical parameters of the samples were characterized by XRD, XPS, ESR, H-2-TPR, NO-TPO, and NO-TPD techniques. Moreover, the CO-deNO mechanisms for the representative catalysts were investigated by in situ DRIFTS. The SO2 and H2O resistances, and their corresponding mechanisms, were also systematically investigated. The catalytic activity testing shows that the optimized molar ratio of Cu, Ce, and Fe is 1:0.5:1.5. At this ratio, the CO-deNO efficiency is highest, but the N2O selectivity is also relatively high. Increasing the Fe percentage could reduce the N2O concentration. The characterization indicates that, at the optimized ratio, the interaction between Fe and Cu is at its strongest, which could increase the formation probability of surface synergistic oxygen vacancies. The Ce existing in the catalysts plays a key role in the adsorption of NO and CO. Moreover, the increasing percentage of Fe could enhance the adsorption and dissociation of NO, and promote the evolution of CO, which can compensate for the effects of the weaker interaction. The NO and CO evolution pathway runs as follows: NO -> M-NO2 -> NO2- -> M-N2O/NO3- -> N2O/N-2; CO -> COO- -> CO32- -> CO2. The H2O and SO2 resistance tests suggest that the appropriate incremental increase in Fe percentage will increase the SO2 or H2O resistance, with the underlying mechanism being that Fe inhibits the formation of sulfates and produces more water adsorption sites, and the increasing Fe percentage would optimize the pore structure.