Advancing oxygen separation: insights from experimental and computational analysis of La0.7Ca0.3Co0.3Fe0.6M0.1O3−δ (M = Cu, Zn) oxygen transport membranes
Guoxing Chen,Wenmei Liu,Marc Widenmeyer,Xiao Yu,Zhijun Zhao,Songhak Yoon,Ruijuan Yan,Wenjie Xie,Armin Feldhoff,Gert Homm,Emanuel Ionescu,Maria Fyta,Anke Weidenkaff
DOI: https://doi.org/10.1007/s11705-024-2421-5
IF: 4.803
2024-04-18
Frontiers of Chemical Science and Engineering
Abstract:In this study, perovskite-type La 0.7 Ca 0.3 Co 0.3 Fe 0.6 M 0.1 O 3− δ (M = Cu, Zn) powders were synthesized using a scalable reverse co-precipitation method, presenting them as novel materials for oxygen transport membranes. The comprehensive study covered various aspects including oxygen permeability, crystal structure, conductivity, morphology, CO 2 tolerance, and long-term regenerative durability with a focus on phase structure and composition. The membrane La 0.7 Ca 0.3 Co 0.3 Fe 0.6 Zn 0.1 O 3 − δ exhibited high oxygen permeation fluxes, reaching up to 0.88 and 0.64 mL·min −1 cm −2 under air/He and air/CO 2 gradients at 1173 K, respectively. After 1600 h of CO 2 exposure, the perovskite structure remained intact, showcasing superior CO 2 resistance. A combination of first principles simulations and experimental measurements was employed to deepen the understanding of Cu/Zn substitution effects on the structure, oxygen vacancy formation, and transport behavior of the membranes. These findings underscore the potential of this highly CO 2 -tolerant membrane for applications in high-temperature oxygen separation. The enhanced insights into the oxygen transport mechanism contribute to the advancement of next-generation membrane materials.
engineering, chemical