Abstract:The Zr0.84Y0.16O1.92 (YSZ)–La0.8Sr0.2Cr0.5Fe0.5O3−δ (LSCrF) composite membrane was prepared using the phase inversion tape casting method. Two slurries, one composed of YSZ and LSCrF powder, and the other composed also graphite, were used for preparation of the membrane. They were co-tape cast onto a Mylar sheet, and then immersed in a water bath for solidification into a green tape through phase inversion mechanism. After sintering at 1450°C in the air, the green tape was converted into a ceramic membrane. The sintered membrane possessed an asymmetric structure: a dense layer of thickness ~30μm and a finger-like porous support of thickness ~1mm. The membrane was further modified by applying a porous YSZ–LSCrF layer on its surfaces at the dense layer side and depositing Sm0.2Ce0.8O2 nano-particles on the inner surfaces of the support. The oxygen permeability of the as-prepared membrane was measured by exposing its dense layer side to air and the support side to CO at elevated temperatures. The membrane exhibited desired oxygen permeability under the given measurement conditions. An oxygen permeation flux as large as 2.4ml·cm−2·min−1 (STP) was observed at 900°C, which is comparable to the hollow fiber membrane of the same composition. Owing to its desired oxygen permeability and good stability, the supported planar YSZ–LSCrF membrane developed in the present study holds promise for applications in chemical reactors integrating oxygen separation and oxygen-consuming chemical reactions such as partial oxidation of methane (POM). The phase inversion tape casting method explored in the present study can be applied to the preparation of other ceramic membranes.

Optimization of Thermochemical Stability of La-based/Zr-based Dual-Phase Composites for Oxygen Transport Membranes via Computational Thermodynamics

Novel Approach for Developing Dual-Phase Ceramic Membranes for Oxygen Separation through Beneficial Phase Reaction

Stability and Oxygen Permeation Behavior of Ce0.8Sm0.2O2−δ–La0.8Sr0.2CrO3−δ Composite Membrane under Large Oxygen Partial Pressure Gradients

Sandwich-like Symmetric Dual-Phase Composite Membrane with an Ultra-Thin Oxygen Separation Layer and Excellent Durability

Effects Of B-Site Doped Elements In The Electronic-Conducting Perovskite Phase On The Property Of Dual-Phase Membranes

Investigation of Co–doped Ce0.8Sm0.2O2–δ–Ba0.95La0.05Zr0.1Fe0.9–xCoxO3–δDual–phase Oxygen Transport Membranes

Advancing oxygen separation: insights from experimental and computational analysis of La0.7Ca0.3Co0.3Fe0.6M0.1O3−δ (M = Cu, Zn) oxygen transport membranes

Materials Design for Ceramic Oxygen Permeation Membranes: Single Perovskite Vs. Single/double Perovskite Composite, a Case Study of Tungsten-Doped Barium Strontium Cobalt Ferrite

Evaluation of La0.7Ca0.3Cr0.95Zn0.05O3–δ–Gd0.1Ce0.9O2–δ Dual-phase Material and Its Potential Application in Oxygen Transport Membrane

Phase Inversion Tape Casting and Oxygen Permeation Properties of Supported Planar Zr0.84Y0.16O1.92–La0.8Sr0.2Cr0.5Fe0.5O3 − Δ Composite Membrane

Synthesis, Oxygen Permeability, and Structural Stability of BaCo0.7Fe0.3−xZrxO3−δ Ceramic Membranes

Ba(Sr) Zr(CoFe) O 3-particle-dispersed Ba 0.5Sr 0.5Co 0.8Fe 0.2O 3-δ mixed conductor composite

Preparation and characterization of supported planar Zr0.84Y0.16O1.92–La0.8Sr0.2Cr0.5Fe0.5O3−δ composite membrane

Preparation and Characterization of Supported Planar Zr0.84Y0.16O1.92–La0.8Sr0.2Cr0.5Fe0.5O3− Composite Membrane

Enhancing the Oxygen Permeation Rate of Zr0.84Y0.16O1.92–La0.8Sr0.2Cr0.5Fe0.5O3−δ Dual-Phase Hollow Fiber Membrane by Coating with Ce0.8Sm0.2O1.9 Nanoparticles

Thermochemical compatibility between La2(Ce1-xZrx)2O7 and 4 mol% Y2O3 stabilized zirconia after high temperature heat treatment

Compressive-Strain-Facilitated Fast Oxygen Migration with Reversible Topotactic Transformation in La 0.5 Sr 0.5 CoO x via All-Solid-State Electrolyte Gating

Oxygen Permeation Through a Ce0.8Sm0.2O2−δ–La0.8Sr0.2CrO3−δ Dual-Phase Composite Membrane

Thermal stability and oxygen separation properties of SrCo0.8Fe0.2O3-delta and SrCo0.8Fe0.1Sn0.1O3-delta ceramic membranes

Effect of Zr4+ Doping on the Oxygen Stoichiometry and Phase Stability of SrCo0.8Fe0.2O3−δ Oxygen Separation Membrane

High-flux dual-phase percolation membrane for oxygen separation