Size Effects in Indentation Measurements of Zr–1Nb–0.05Cu Alloy

Chunguang Yan,Rongshan Wang,Yanli Wang,Xitao Wang,Zhi Lin,Guanghai Bai,Yanwei Zhang
DOI: https://doi.org/10.1016/j.msea.2015.01.024
2015-01-01
Abstract:Indentation size effects (ISEs) have been studied in both indentation hardness measurement and indentation creep process of Zr–1Nb–0.05Cu. The continuous stiffness measurement (CSM) technique was used to determine hardness up to 2000nm. The indentation creep tests were performed at room temperature with nominal initial depth from 100 to 2000nm. It is shown that the hardness, activation energy and activation volume are all dependent on the indenter displacement. The ISE of indentation hardness relates to the theory of strain gradient plasticity. The course of activation volume versus hardness reflects the mechanism transition of indentation creep. For small indents, the diffusion through dense dislocations dominates the creep behavior. When the indents get larger, the deformation is governed by dislocation glide.
What problem does this paper attempt to address?