Abstract:In this study, 5083 aluminum alloys modified with grain refiner, 0.25% Zr and 0.46% Mn, were processed by reciprocating extrusion to yield high-strain-rate superplasticity above 400°C and superior room-temperature mechanical properties. Without any prior homogenization treatment, 10 extrusion passes could give the cast billets an equiaxed grain structure with a grain size of about 4.5μm and a subgrain size about 0.2μm, and a uniform distribution of fine inclusions and dispersoids in the matrix. The fine-grained structure was stable up to 525°C, giving the alloy a high-strain-rate and low-stress superplasticity over a wide operating temperature of 400–500°C. In the tensile test at 500°C, a maximum elongation of 1013% and a low flow stress of 7.7MPa at 5×10−2s−1 were achieved. The apparent and true activation energies for low temperatures (300–400°C) without high-strain-rate superplasticity were 220.6 and 208kJ/mol, respectively, whereas those at high temperatures (400–500°C) were 88.4 and 98.7kJ/mol, respectively. Further analysis confirms that grain boundary sliding is the dominant mechanism over the high-strain-rate region from 1×10−2 to 5×10−1s−1 at 500°C, and power-law breakdown mechanism occurs over the strain rate from 5×10−4 to 1×10−2s−1 at 300°C. The high-strain-rate superplasticity was more strongly enhanced by Zr addition than addition of Cr and Mn. Two enhancing mechanisms for the maximum superplastic elongation and the optimum strain rate are proposed. This study concludes that the effectiveness of Zr is caused by the fineness and the coherency of Zr-rich dispersoids in the matrix.

Achieving High Superplasticity of a New Al–Mg–Sc–Zr Alloy Sheet Prepared by a Simple Thermal–mechanical Process

Superplastic Behavior and Microstructure Evolution of A New Al-Mg-Sc-Zr Alloy Subjected to A Simple Thermomechanical Processing

Excellent High Strain Rate Superplasticity of Al-Mg-Sc-Zr Alloy Sheet Produced by an Improved Asymmetrical Rolling Process

Superplasticity Behaviors of Al-Zn-Mg-Zr Cold-Rolled Alloy Sheet with Minor Sc Addition

Excellent superplasticity and deformation mechanism of Al–Mg–Sc–Zr alloy processed via simple free forging

High Strain Rate Superplasticity in an Al–Mg–Sc–Zr Alloy Processed Via Simple Rolling

Effect of Sc and Zr Additions on Grain Stability and Superplasticity of the Simple Thermal–mechanical Processed Al–Zn–Mg Alloy Sheet

Achieving high strain rate superplasticity of an Al-Mg-Sc-Zr alloy by a new asymmetrical rolling technology

Achieving high superplasticity of a traditional thermal–mechanical processed non-superplastic Al–Zn–Mg alloy sheet by low Sc additions

Achieving high strain rate superplasticity in an Al-Cu-Li alloy processed by thermo-mechanical processing

Superplastic Behavior of an Al–Mg–Li Alloy

Superplasticity of Mg-5.8Zn-1Y-Zr Alloy Sheet Fabricated by Combination of Extrusion and Hot-Rolling Processes

On Mechanical Properties and Superplasticity of Mg–15Al–1Zn Alloys Processed by Reciprocating Extrusion

Superplastic Behavior of Al-Cu-Li Based Alloy

Grain Refinement and Superplastic Behavior of 1420 Al-Li Alloy Sheets

Superplasticity of 5083 Alloys with Zr and Mn Additions Produced by Reciprocating Extrusion

High Strain Rate Superplasticity in Al-Zn-Mg-Based Alloy: Microstructural Design, Deformation Behavior, and Modeling

High Strain Rate Superplasticity in a Micro-grained Al{Mg{Sc Alloy with Predominant High Angle Grain Boundaries

Achieving Superplasticity in AZ31 Magnesium Alloy Processed by Hot Extrusion and Rolling

Superplasticity of Fine-Grained AZ31 Mg Alloy Sheets

Superplastic Behavior and Microstructure Evolution of a Fine-Grained Mg-Nd-Zn-Zr Alloy Processed by Hot Extrusion