Abstract:In this study, the effect of heat treatment and yttrium additions on the microstructure, mechanical properties, and tribological behavior of Al-15% Mg2Si cast composites was investigated. The microstructural study revealed the presence of both primary and secondary Mg2Si phases in all composite specimens and also Y-containing intermetallics (Al2Y phases) at higher concentrations. It was also found that Y addition does not change the size and morphology of primary Mg2Si particles considerably, but the pseudo-eutectic Mg2Si changed from a flake-like morphology to fine fibrous or rod-like one. The results show that proper content of Y additions can reduce the amount of Mg2Si phase through dissolving it into the matrix, lead to the precipitation of Al2Y phase and improve the mechanical properties. Modified composites with 0.5% Y exhibited an ultimate tensile strength (UTS) of 290 MPa with an elongation of 4.3%. After exposing the composite to solution treatment at 520 °C for 4 h, the tensile strength of the composite continuously increased with the increase of Y content, and reached the maximum at 1% Y. The maximum UTS and elongation at room temperature for the heat-treated composites are 294 MPa and 7.4%, respectively. In the cast specimen, fracture surfaces are covered by packets with coarse steps, suggesting a brittle mode of failure. Modified composites with 0.5 wt.% Y contain several cracked particles together with a few decohered primary Mg2Si particles. In solution heat-treated state, dimples present at the fracture surface are rather coarse but homogenous, showing a semi-ductile mode of fracture. Wear test results showed that the wear resistance of all specimens increases with the addition of Y up to 0.3 wt.%. Scanning electron microscopic observations of the worn surfaces revealed that the dominant wear mechanism was abrasive wear accompanied by some delamination wear mode.

Effect of Y Content on Interfacial Microstructures and Mechanical Properties of C-F/Mg Composite

Effect of Y addition on the interfacial microstructures and mechanical properties of C f /Mg composites

Effect of Gd Content on Interfacial Microstructures and Mechanical Properties of C-F/Mg Composite

Interfacial microstructure and strengthening mechanisms of Cf/Mg composite with double-layer interface

Effects of Y on Microstructure and Mechanical Properties of Extruded Mg-5Al-1Ca Magnesium Alloys

Effects of the Rare Earth Y on the Structural and Tensile Properties of Mg-based Alloy: A First-Principles Study

Effects of rare-earth additions on the microstructure and strength of Cu–Ag composites

Effect of Y content on microstructure and mechanical properties of as-cast Mg–8Li–3Al–2Zn alloy with duplex structure

Study on the Fine Grain Size and Microhardness at the Interface of AZ31/Mg‐Y Composites

Effects of interfacial diffusion induced infiltration process on the microstructure evolution and interfacial enhancement of CF/Mg composites

Effects of Y Content on Microstructure and Properties of Mg-Y-Zn-Zr Alloy

Mechanical and Tribological Characterization of Al-Mg2Si Composites after Yttrium Addition and Heat Treatment

Simulation on Microstructure Evolution and Mechanical Properties of Mg−Y Alloys: Effect of Trace Y

Microstructure and Mechanical Properties of Mg-Y Alloys

Effect of Y content on microstructure evolution and tensile properties of Mg-8Li-3Al-2Sn-xY alloys

Bonding Interface Zone of Mg-Gd-Y/Mg-Zn-Gd Laminated Composite Fabricated by Equal Channel Angular Extrusion

Effects of Yttrium on Microstructure and Mechanical Properties of Mg-6Al Magnesium Alloy

Effect of combined addition of Zr, Ti and Y on microstructure and tensile properties of an Al-Zn-Mg-Cu alloy

Effects of Ca and Y on microstructures and mechanical properties of magnesium alloy AZ81

Influence of Y on Mechanical Properties of Mg Alloy AZ91

Effect of Y Concentration on the Microstructure and Mechanical Properties of As-Cast Mg–Zn–Y–Zr Alloys