MICROSTRUCTURE AND PROPERTIES OF TiB 2 – TiAl COMPOSITES SHEETS PREPARED BY FOIL METALLURGY
X. P. Cui,L. Geng,G. H. Fan,J. X. Gong,K. Fang
2013-01-01
Abstract:Detailed microstructure and mechanical properties of innovative TiB2-TiAl composite sheet prepared by hot rolling of Ti-(TiB2/Al) laminates and subsequent reaction annealing has been systemically investigated. The TiB2-TiAl composite show a typical micro-laminated structure consisting of lamellar TiAl layers and TiB2-rich layers. Tensile properties testing shows that with increasing temperature from ambient temperature to 700C, the tensile properties have a sharp increase because of an increase of energy dissipation by plastic deformation and the reduction of the sensitivity to microcrack formation. It is noteworthy that the fracture toughness has significantly improved and the highest value is 15.6 MPa·m, which approaches that of TiAl reinforced with TiNb fiber. Toughening mechanism contains crack deflection caused by TiB2-rich layers, crack branching and TiB2-rich/TiAl interface delamination. 1 General Introduction Gamma-TiAl (γ-TiAl) alloys have great potential for aerospace and automotive applications because of their attracted properties and thus are considered as one of the most promising lightweight hightemperature structural materials [1, 2]. Recently, much attention has been paid to the production of γTiAl alloys sheets or foils, which is suitable for thermal protection or exhaust honeycomb structures [3, 4]. However, owing to the limited ductility and poor workability of γ-TiAl , γ-TiAl sheets or foils can be only manufactured above 1100C with extremely low strain rate [5, 6]; furthermore, relatively expensive equipment and specialized pack materials are required. Therefore, researchers have exploited elemental foil metallurgy technique [1, 79]: pure Ti and Al elemental foils with excellent plastic deformability are stacked to obtain Ti-Al laminates and the laminates are subsequently reaction annealed to produce monolithic γ-TiAl sheets. One of the most significant advantages of this method is to avoid the direct deformation and processing of brittle TiAl-based alloys bullets and can realize the near-net-shape forming of TiAl-based sheets. However, the relative density and mechanical properties of final monolithic TiAl are rather low; in particular, the high temperature strength can not satisfy the requirement for aerospace applications. Therefore, TiB2/Al composite foils were utilized to replace pure Al foils and Ti-(TiB2/Al) laminates were manufactured by hot rolling, and subsequent multi-step reaction annealing were employed to produce micro-laminated TiAl matrix composite sheets which can combine respective advantages of intermetallic compounds and ceramic particles. Furthermore, the laminated composites can dramatically improve many properties including the improvement of crack propagation resistance and/or provide enhanced high temperature strength because of the multi-interface effects [10-12]. However, the microstructure of innovative micro-laminated TiAl matrix composite sheets need to further observation and up to now, few investigations focus on the mechanical properties of the innovative microlaminated TiB2–TiAl composite sheets. In the present work, the microstructures of TiB2–TiAl composite sheets with unique micro-laminated structure are investigated in detail and the hightemperature tensile properties and fracture toughness have been studied, with the emphasis on the relationship between mechanical properties and micro-laminated structure. 2 Experimental Procedures Thin commercial pure Ti foils with thickness of 200μm and in-house fabricated 5 vol. % TiB2/Al (Al matrix with 99.7% purity) composite sheets with the thickness of 200 μm were cut into 50 mm × 50 mm squares. Surface pre-treated Ti and TiB2/Al sheets were alternately stacked to form a “sandwich” and encapsulated in Al alloys packing and then hotrolled at 510 C with a 60% reduction in thickness to produce Ti-(TiB2/Al) laminates, the microstrucutre of hot-rolled sample is shown in Fig. 1. The laminates were annealed in a vacuum furnace as follows: i) initial annealing at 1200 C for 20min under 0.1 MPa to completely consume Al and obtain TiAl3 phases and subsequent densification treatment in vacuum (~10 Pa) under 50 MPa at 1260 C for 2h to enclose the Kirkendall voids formed during the initial annealing process; ii) second annealing for composition homogenization at 1250 C for 15h; iii) final annealing at 1400 C for 15 min in order to obtain TiAl matrix with the lamellar structure consisting of alternating γ-TiAl and α2-Ti3Al. The final thickness of the micro-laminated TiB2-TiAl composite sheets is in the range of 3.0–3.2 mm. Microstructure observation, chemical composition analysis and phase identification of the final microlaminated TiB2–TiAl composite sheets containing different contents of TiB2 were carried out using scanning electron microscopy (SEM, FEI Quanta 200F) equipped with energy dispersive X-ray spectrometer (EDX) and a transmission electron microscope (TEM, FEI Tecnai F30, 200kv). All SEM images were taken in the back-scattered electrons (BSE) mode. In addition, X-ray diffraction (XRD) was used to identify different phases. All the samples are examined in the rolling direction (RD) – normal direction (ND) plane. Mechanical properties of the final micro-laminated TiB2–TiAl composite sheets were evaluated by tensile testing at ambient and 700C and room temperature fracture toughness testing. The tensile samples were cut parallel to the rolling direction using electrical discharge machining (EDM) and their surfaces were carefully polished to remove the machining traces. The cross-section of tensile samples was 2.5 mm × 1.5 mm and the gauge length was 15mm. The tensile tests were carried out at room temperature and 700C with an Instron-1186 universal testing machine with the initial strain rate of 1.3 × 10 s. The samples were mechanically polished using 00-grade silicon carbide papers to remove surface scratches prior to testing. The fracture toughness measurement was carried out using three-point bend tests on the single edge notched bend (SENB) specimens with the dimensions of 20 mm × 4 mm × 2 mm where the loading span is 16 mm. The straight notch was introduced at the center part of the test bar using a 100 μm wide diamond blade with a notch depth of 0.5 W (the width of the specimen). Two types of fracture toughness specimens with notch orientation parallel to TD and ND were prepared, as shown in Figure 2. Fracture surfaces of tensile specimens and the crack initiation and propagation also examined using a scanning electron microscope. Fig. 1. Microstructure of the hot-rolled Ti-(TiB2/Al) laminates (a) the multi-layered structure consisting of alternating Ti layer and TiB2/Al layer; (b) showing the excellent interfacial bonding and no intermetallic compounds formation at the interface between Ti layer and TiB2/Al layer Fig. 2. Two types of fracture toughness specimens with notch orientation in the parallel to (a) transverse direction (TD); (b) normal direction (ND) THE 19 INTERNATIOANAL CONFERENCE ON COMPOSITE MATERIALS 3 Results and Discuss 3.1 Microstructure features The multi-layered Ti–(TiB2/Al) laminates are subjected to roll bonding and subsequent four-stage annealing between 660 C and 1400 C is used to prpduce the TiAl matrix composite sheets. XRD pattern of the resulting TiAl matrix composite is shown in Fig. 2(a), indicating the presence of the close-packed hexagonal Ti3Al with DO19 structure and TiB2 and the tetragonal L10 TiAl. This implies TiB2 particles do not participate in any reaction and are completely retained. Fig. 3. X-ray diffraction (XRD) pattern of resulting micro-laminated TiB2-TiAl composite sheets The detailed microstructure features of the resulting composite sheets are shown in Fig. 4. As shown in Fig. 4, the resulting composite sheet displays a typical multi-layered structure consisting of TiB2 particles stacking layer (denoted as TiB2-rich layer) with 5μm wide and TiAl layer with an average width of 120μm. TEM images shown in Fig. 5(a) including the inset indicate that TiB2-rich layer is actually composed of numerous TiB2 particles and a small quantity of TiAl. The interfacial bonding between TiB2 particles and TiAl is rather compact and no voids are found within TiB2-rich layers. According to SEM/EDX, the compositions of TiAl layer contain 47.2-53 at. % Ti and the remaining content of Al, which corresponds to lamellar (α2-Ti3Al+γTiAl) phase. Representative microstructure of lamellar (α2-Ti3Al+γ-TiAl) layer is shown in Fig. 5(b). As shown in Fig. 4 and Fig. 5, the size of (α2+γ) lamellar colony is between 70μm and 150μm with an average value of 100μm and the average spacing of γ-TiAl and α2-Ti3Al lamellae is 150 nm, and γTiAl and α2-Ti3Al follows the orientation relationship: [11-20]α2//[1-10]γ and (0001)α2//(111)γ. The lamellar colony size is much smaller than that in the γ-TiAl alloys produced by conventional casting technique (approximately 500 μm–several mm) [13, 14]. This is because the TiB2-rich layer significantly hinders the growth of the lamellar colony. It is noteworthy that the thickness ratio of TiB2-rich and TiAl layers can be conveniently adjusted by varying the volume fraction of TiB2 in TiB2/Al composite and the respective thickness of TiB2/Al composite foils and commercial pure Ti foils. Consequently, the microstructures of novel micro-laminated TiB2– TiAl composite sheets can be devised and controlled by accommodating the thickness of pure Ti foils and TiB2/Al composite foils and the volume fraction of the reinforcement TiB2 particles in TiB2/Al composite foils. Therefore, TiB2–TiAl composite sheets with novel micro-laminated structure can be successfully fabricated using roll bonding and subsequent reaction annealing of Ti-(TiB2/Al) laminate. Fig. 4. (a) representative backscattered electron images of micro-laminated TiB2TiAl composite sheets; (b) the interface between TiB2-rich layer and fully lamellar TiAl layer Fig. 5. (a) TEM images and selected area electron d