Atom probe tomography study of Mg-dependent precipitation of Ω phase in initial aged Al-Cu–Mg–Ag alloys

song bai,xuanwei zhou,zhiyi liu,puyou ying,meng liu,sumin zeng

DOI: https://doi.org/10.1016/j.msea.2015.04.052

2015-01-01

Abstract:The association between Mg variations and the precipitation of Ω phase in Al–Cu–Mg–Ag alloys were investigated by transmission electron microscopy and quantitative atom probe tomography analysis. After aging at 165°C for 2h, the highest number density of Ω phase was revealed in 0.81Mg alloy, leading to the highest strength properties. The lowest strength properties of 0.39Mg alloy was related to the lowest precipitation kinetics of Ω phase. The parabolic change in the plate number density with increasing Mg highlighted the existence of a critical Mg content that contributed to the strongest precipitation kinetics of Ω phase. The number density of Mg–Ag co-clusters was not the sole factor in controlling the Ω precipitation. It was found that the precipitation of Ω phase was not only determined by initial Mg–Ag co-clustering but also related to the effective competition for solutes. In addition, the cluster-dominated microstructure facilitated the dense precipitation of Ω phase.