Abstract:Purpose: In this work, tension, impact, bend and fatigue tests were conducted in an AM60 magnesium alloy. The effects of environmental temperature and loading rates on impact and tension behavior of the alloy were also investigated. Design/methodology/approach: The tests were conducted using an Instron universal testing machine. The loading speed was changed from 1 mm/min to 300 mm/min to gain a better understanding of the effect of strain rate. To understand the failure behavior of this alloy at different environmental temperatures, Charpy impact test was conducted in a range of temperatures (-40~35°C). Plane strain fracture toughness (KIC) was evaluated using compact tension (CT) specimen. To gain a better understanding of the failure mechanisms, all fracture surfaces were observed using scanning electron microscopy (SEM). In addition, fatigue behavior of this alloy was estimated using tension test under tension-tension condition at 30 Hz. The stress amplitude was selected in the range of 20~50 MPa to obtain the S-N curve. Findings: The tensile test indicated that the mechanical properties were not sensitive to the strain rates applied (3.3x10-4~0.1) and the plastic deformation was dominated by twining mediated slip. The impact energy is not sensitive to the environmental temperature. The plane strain fracture toughness and fatigue limit were evaluated and the average values were 7.6 MPa.m1/2 and 25 MPa, respectively. Practical implications: Tested materials AM60 Mg alloy can be applied among others in automotive industry aerospace, communication and computer industry. Originality/value: Many investigations have been conducted to develop new Mg alloys with improved stiffness and ductility. On the other hand, relatively less attention has been paid to the failure mechanisms of Mg alloys, such as brittle fracture and fatigue, subjected to different environmental or loading conditions. In this work, tension, impact, bend and fatigue tests were conducted in an AM60 magnesium alloy.

Weibull Statistical Analysis of the Effect of Melt Conditioning on the Mechanical Properties of AM60 Alloy

Melt Superheating on the Microstructure and Mechanical Properties of Diecast Al-Mg-Si-Mn Alloy

Microstructure and Mechanical Properties of Thin-Wall and High-Rib Parts of AM60B Mg Alloy Formed by Double Control Forming and Die Casting under the Optimal Conditions

Effect of Solutionising and Ageing on the Microstructure and Mechanical Properties of a High Strength Die-Cast Al–Mg–Zn–Si Alloy

Microstructure and Mechanical Properties of Melt-Conditioned High-Pressure Die-Cast Mg-Al-Ca Alloy

Experimental study of squeeze casting of ZK60 magnesium alloy

Investigation on Mechanical Behaviour of AM60 Magnesium Alloys

Study on Plastic Constitutive Relation and Ductile Fracture Criterion of AM60B Magnesium Alloy

Effect of Alloying with Al, Nd and Ca and Heat Treatment on Microstructures and Mechanical Properties of Vacuum Die-Cast AM50 Alloy

Influence of Processing Parameters on Microstructure and Mechanical Properties of Die Casting AM50 Alloy

On the Deformation Behavior of Heterogeneous Microstructure and Its Effect on the Mechanical Properties of Die Cast AZ91D Magnesium Alloy

Influence of Strain Rate and Stress State on the Mechanical Behavior of Die-Casting AM60 Magnesium Alloy

MELT CONDITIONED HIGH PRESSURE DIE CASTING (MC-HPDC) OF Mg-ALLOYS

Microstructure Characteristics of the Eutectics of Die Cast AM60B Magnesium Alloy

Melt-Conditioned, High-Pressure Die Casting of Mg–Zn–Y Alloy

The Small Fatigue Crack Growth Behavior of an AM60 Magnesium Alloy

The Correlation Between Microstructure and Mechanical Properties of High-Pressure Die-Cast AM50 Alloy

Effect of process parameters on microstructure and properties of AM50A magnesium alloy parts formed by double control forming

Microstructure and mechanical properties of low pressure die cast AM50 magnesium alloy

Corrosion and Residual Strength Analysis of High Pressure Die Casting AM Series Mg Alloys

Effect of solidification conditions on microstructure, mechanical and wear properties of Mg–5Al–3Ca–0.12Sr magnesium alloy