Abstract:Diphenyl carbonate (DPC) and diphenyl ketone (DPK) were used as diluents to prepare microporous polyvinylidene fluoride (PVDF) membranes via thermally induced phase-separation (TIPS) method. The liquid - liquid phase-separation phenomena were found in PVDF/DPC and PVDF/DPK systems during the thermally induced phase-separation processes. The monotectic points of PVDF/DPC and PVDF/DPK systems appeared at PVDF concentration approximately 30 and 56 %(wt), respectively. This suggested that PVDF membrane with a bicontinuous or cellular structure could be obtained when the PVDF concentration was less than the point values. The effects of polymer concentration and quenching temperature on the membrane structure, porosity, and tensile strength were also investigated. The results showed that low polymer concentration and high quenching temperature led to a large pore size membrane. The tensile strength of the membrane increased with the increase of the polymer concentration, but the porosity of the membrane decreased. On condition that the PVDF concentration was higher than monotectic points, only polymer crystallization occurred and a typical compact spherulitic structures were obtained. Moreover, a binary diluent of DPK and secondary solvent such as 1,2-propylene glycol (PG) was used to replace the single diluent in TIPS process. The phase diagram for the PVDF/binary diluent of DPK and PG system was measured in the range of the PG/DPK mass ratio changing from 0 to 2/3. Then the effects of the PG/DPK mass ratio and the PVDF concentration on membrane cross-section structures and tensile strength were also investigated. The results showed that the addition of PG brought about a shift of the cloud point curve to a higher temperature and the extension of the liquid-liquid phase separation region to a higher polymer concentration. Therefore a bicontinuous cross-section structure was obtained when the PG/DPK mass ratio was 3/7 and the polymer concentration was 30 wt%. As an increase of the PG/DPK mass ratio, the tensile strength increased gradually at a fixed PVDF concentration. Moreover, for the same PG/DPK mass ratio, the cross-section microstructure changed from a bicontinuous or a cellular structure to a spherulitic structure, and the tensile strength increased drastically as the polymer concentration increased from 20 wt% to 50 wt%. According to the properties of diluents, the industrial scale production line with a twin-screw extruder of microporous PVDF hollow fiber membranes was established and a series of different type hollow fiber membranes were prepared for the corresponding applications of pressure-driven modulus, submersed modulus and membrane bio-reactor modulus. At the same time, the full recycle of diluents was almostly actualized by using a series of unit opertaions such as extraction, distillation, delamination, sedimentation and drying processes. It means there is no waste emission in the preparation of PVDF membranes or it is a green process.

Preparation of A Poly(Vinyl Chloride) Ultrafiltration Membrane Through the Combination of Thermally Induced Phase Separation and Non-Solvent-Induced Phase Separation

Preparation of Porous PVDF Membrane Via Thermally Induced Phase Separation with Diluent Mixture of DBP and DEHP

Preparation of Positively-Charged Blend PVC/PEI Ultrafiltration Membranes with Crosslink Structure for Dye/Salt Separation

Preparation of High Density Polyethylene/polyethylene- Block -Poly(ethylene Glycol) Copolymer Blend Porous Membranes Via Thermally Induced Phase Separation Process and Their Properties

Preparation of PVDF membrane via synergistically vapor and non-solvent-induced phase separation

Pore Size Tailoring from Ultrafiltration to Nanofiltration with PVC-g-PDMA Via Rapid Immersion Thermal Annealing

Morphology and Formation Mechanism of Poly(Vinylidene Fluoride) Membranes Prepared with Immerse Precipitation: Effect of Dissolving Temperature

Green preparation of polyvinylidene fluoride microfiltration membranes via thermally indueced phase separation method using diphenyl carbonate and diphenyl ketone as diluents

Preparation and Characterization of Microporous PVDF Membrane by Thermally Induced Phase Separation from a Ternary Polymer/solvent/non-Solvent System

Membranes of poly (vinyl butyral) (PVB) or cationic PVB (CPVB) blended with poly (vinylidene fluoride) (PVDF) prepared by a nonsolvent induced phase separation method: Miscibility and hydrophilicity

The Polymer-rich Phase Solidification Process of PVDF-PVP-DMAc-H2O Solution

Poly(vinyl chloride) (PVC) hollow fiber ultrafiltration membranes prepared from PVC/additives/solvent

Influence of Blending Ratio and Polymer Concentration on Miscibility of PVC/PVB and Property & Structure of Flat Ultra-Filtration Membrane

Preparation of microporous poly(vinylidene fluoride)hollow fiber membranes via thermally induced phase separation

Preparation of PVDF membranes via the low-temperature TIPS method with diluent mixtures: The role of coagulation conditions and cooling rate

Fabrication of PVDF ultrafiltration membrane using modified thermally induced phase separation: The role of amphiphilic and hydrophilic non-solvents

PVDF Membrane Formation Via Thermally Induced Phase Separation

Preparation and Properties of Ultra High Molecular Weight Polyethylene/High Density Polyethylene Microporous Membrane via Thermal Induced Phase Separation

Preparation of Polyvinylidene Fluoride (pvdf) Membranes Via Nonsolvent Induced Phase Separation Process Using A Tween 80 and H2o Mixture As an Additive

Fabrication of Polyvinyl Chloride Ultrafiltration Membranes with Stable Antifouling Property by Exploring the Pore Formation and Surface Modification Capabilities of Polyvinyl Formal

Preparation and Characterization of PVDF Flat Sheet Microporous Membrane via Thermally Induced Phase Separation