Abstract:Diphenyl carbonate (DPC) and diphenyl ketone (DPK) were used as diluents to prepare microporous polyvinylidene fluoride (PVDF) membranes via thermally induced phase-separation (TIPS) method. The liquid - liquid phase-separation phenomena were found in PVDF/DPC and PVDF/DPK systems during the thermally induced phase-separation processes. The monotectic points of PVDF/DPC and PVDF/DPK systems appeared at PVDF concentration approximately 30 and 56 %(wt), respectively. This suggested that PVDF membrane with a bicontinuous or cellular structure could be obtained when the PVDF concentration was less than the point values. The effects of polymer concentration and quenching temperature on the membrane structure, porosity, and tensile strength were also investigated. The results showed that low polymer concentration and high quenching temperature led to a large pore size membrane. The tensile strength of the membrane increased with the increase of the polymer concentration, but the porosity of the membrane decreased. On condition that the PVDF concentration was higher than monotectic points, only polymer crystallization occurred and a typical compact spherulitic structures were obtained. Moreover, a binary diluent of DPK and secondary solvent such as 1,2-propylene glycol (PG) was used to replace the single diluent in TIPS process. The phase diagram for the PVDF/binary diluent of DPK and PG system was measured in the range of the PG/DPK mass ratio changing from 0 to 2/3. Then the effects of the PG/DPK mass ratio and the PVDF concentration on membrane cross-section structures and tensile strength were also investigated. The results showed that the addition of PG brought about a shift of the cloud point curve to a higher temperature and the extension of the liquid-liquid phase separation region to a higher polymer concentration. Therefore a bicontinuous cross-section structure was obtained when the PG/DPK mass ratio was 3/7 and the polymer concentration was 30 wt%. As an increase of the PG/DPK mass ratio, the tensile strength increased gradually at a fixed PVDF concentration. Moreover, for the same PG/DPK mass ratio, the cross-section microstructure changed from a bicontinuous or a cellular structure to a spherulitic structure, and the tensile strength increased drastically as the polymer concentration increased from 20 wt% to 50 wt%. According to the properties of diluents, the industrial scale production line with a twin-screw extruder of microporous PVDF hollow fiber membranes was established and a series of different type hollow fiber membranes were prepared for the corresponding applications of pressure-driven modulus, submersed modulus and membrane bio-reactor modulus. At the same time, the full recycle of diluents was almostly actualized by using a series of unit opertaions such as extraction, distillation, delamination, sedimentation and drying processes. It means there is no waste emission in the preparation of PVDF membranes or it is a green process.

Preparation and Characterization of Microporous PVDF Membrane by Thermally Induced Phase Separation from a Ternary Polymer/solvent/non-Solvent System

Preparation of Porous PVDF Membrane Via Thermally Induced Phase Separation with Diluent Mixture of DBP and DEHP

Preparation of porous PVdF membrane via thermally induced phase separation using sulfolane

Preparation of PVDF- HFP Porous Membrane Via Thermally Induced Phase Separation and Application in Lithium Ion Battery

MICROPOROUS PVDF-HFP-BASED POLYMER MEMBRANES FORMED FROM SUPERCRITICAL CO2 INDUCED PHASE SEPARATION *

Preparation and Characterization of PVDF Flat Sheet Microporous Membrane via Thermally Induced Phase Separation

Preparation of PVDF Membranes via TIPS Method: The Effect of Mixed Diluents on Membrane Structure and Mechanical Property

PVDF Membrane Formation Via Thermally Induced Phase Separation

Tributyl Citrate As Diluent for Preparation of Pvdf Porous Membrane Via Thermally Induced Phase Separation

Preparation of PVDF membranes via the low-temperature TIPS method with diluent mixtures: The role of coagulation conditions and cooling rate

Preparation of PVDF-HFP Microporous Membranes via the Thermally Induced Phase Separation Process

Thermally Induced Phase Separation of Poly(vinylidene Fluoride)/diluent Systems: Optical Microscope and Infrared Spectroscopy Studies

Green preparation of polyvinylidene fluoride microfiltration membranes via thermally indueced phase separation method using diphenyl carbonate and diphenyl ketone as diluents

Effect of Preparation Conditions on the Morphology, Polymorphism and Mechanical Properties of Polyvinylidene Fluoride Membranes Formed Via Thermally Induced Phase Separation

Microstructure of Microporous Polyvinylidene Fluoride Membrane Prepared Via Thermally Induced Phase Separation

Poly(vinylidene fluoride) membrane preparation with an environmental diluent via thermally induced phase separation

Preparation and properties of poly (vinylidene fluoride) membranes via the low temperature thermally induced phase separation method

Formation of a Bicontinuous Structure Membrane of Polyvinylidene Fluoride in Diphenyl Carbonate Diluent Via Thermally Induced Phase Separation

Study on Microstructure of PVDF Membrane Formed Via TIPS

Preparation of microporous PVDF membrane via tips method using binary diluent of DPK and PG

Wide Liquid-Liquid Phase Separation Region Enhancing Tensile Strength of Poly(vinylidene Fluoride) Membranes Via TIPS Method with a New Diluent