Abstract:1. Sm211 grains inevitably coarsen and grow epitaxially in the conventional process. Natural Sm211 refinement in Ba‐rich modified precursor powder (BMPP) outperforms the artificial method in conventional precursor powder. 2. In situ formed Sm211 through nucleation catastrophe possesses naturally small size. 3. A 24‐mm SmBCO bulk achieved from BMPP: 51.5 N levitation force, 0.537 T trapped field. Among the REBa2Cu3O7‐δ (REBCO or RE123, RE = rare earth element) family, SmBCO is preferably used in top‐seeded melt‐growth (TSMG) because of its outstanding property and more controllable stoichiometry 123. Nevertheless, the refinement of Sm2BaCuO5 (Sm211) particles has been challenging for high‐performance SmBCO bulks. Conventional precursor powders (SmBa2Cu3O7‐δ plus Sm2BaCuO5) intrinsically result in enlarging Sm2BaCuO5 particles due to their coarsening and epitaxial growth during the heating process. Here, we used modified precursor powders (MPPs, Sm2O3 plus Ba2Cu3O5) in air‐processed TSMG, in which there is neither Sm211 in the beginning nor related enlargement during heating. Consequently, the nucleation catastrophe of Sm211 occurred above the peritectic temperature, which in situ formed, possessing naturally small size. Further, aiming to suppress the Sm/Ba substitution, Ba‐rich MPP, substituting Ba2Cu3O5 with Ba3Cu4O7) was employed, producing an excellent SmBCO bulk with a diameter of 24 mm: levitation force of 51.5 N and trapped field of 0.537 T. Optical micrographs and quantitative analyses confirmed the superior refinement and distribution of Sm211 particles in SmBCO bulks. Most importantly, new strategies in this work are widely applicable for developing cost‐effective and high‐performance other REBCO bulk superconductors.

Effects on Air-Processed Ndbco Superconductor Bulks when Adding A Ba-Rich Nd2ba4cu2o9 Phase

Growth of A High Performance Smbco Bulk Superconductor with the Addition of A Sm2ba4cu2o9 Phase

NdBa2Cu3O7−δ stoichiometry control (at pO2=0.21 atm) and enhancement of superconductivity

Two-layer Batch-Process of YBa2Cu3Ox Bulk Superconductors Induced by NdBa2Cu3Ox Film-Seeds

95 K NdBCO Single Crystal Grown in Air by Controlling Liquid Composition

Preparation of Nb 3 Al Superconductor by Powder Metallurgy and Effect of Mechanical Alloying on the Phase Formation

Large Size And High T-C, J(C) Smbco Bulk Superconductor With Addition Of Sm242 Particles Grown In Air

Melt-textured Growth of NdBCO Bulk Seeded by Superheating NdBCO Thin Film

Large Size and High Performance of a Gd–Ba–Cu–O Bulk Superconductor Grown Using New Approaches

Formation Mechanism of the 3321 Phase in Bi-System High Temperature Superconduting Materials

Study on the Thermal Stability of the NdBCO Film in Inducing the Growth of REBa2Cu3Ox/Ag Superconductor Bulks

Seed-Size Effect on the Growth and Superconducting Performance of Ybco Single-Grain Bulks

NdBCO Melting and Solidification in the Zone Melting Method

Flux Pinning Properties of Single-Grain Bulk GdBCO Superconductors Processed by Different Thicknesses of Y123 Liquid Source

The Effect of Boron on Equilibrium of Superconducting Phases in Bi-Pb-Sr-Ca-Cu-O System

STUDY OF THE MONOCLINIC PHASE AND EFFECT OF Ba-DOPING IN Bi-Sr-Ca-Cu-O SYSTEM

Multi-seeded growth of melt processed Gd–Ba–Cu–O bulk superconductors using different arrangements of thin film seeds

YBCO-buffered NdBCO film with higher thermal stability in seeding REBCO Growth

Study on the NdBCO LPE Thick Film Seed for the Melt-Textured Growth of YBCO and (Y,sm)bco

Growth of Nd-123 Single Crystals with Enhanced Superconducting Properties

Behavior and effect of natural refinement of Sm2BaCuO5 derived from homogeneous nucleation catastrophe in bulks