NdBa2Cu3O7−δ stoichiometry control (at pO2=0.21 atm) and enhancement of superconductivity

Xin Yao,Makoto Kambara,Takateru Umeda,Yuh Shiohara
DOI: https://doi.org/10.1016/S0921-4534(97)01834-0
1998-01-01
Abstract:In the air atmosphere, high superconducting transition temperature (T-c) Nd1+xBa2-xCu3O7-delta (NdBCO) single crystals were grown by top-seeded solution-growth (TSSG). Two controllable thermodynamical parameters, i.e. liquid composition and growth temperature were focused on. Using the ratio of Ba to Cu (Ba:Cu) at 0.78 in the liquid, the grown NdBCO crystal displays onset T-c of 94.6 K with a sharp transition width Delta T less than 1.5 K. The Ba-rich liquid leads to the lower substitution of Ba with Nd in grown crystals, resulting in the higher T-c. This finding suggests that the Ba:Cu ratio in the liquid is a very important processing parameter for obtaining higher T-c of the NdBCO superconductors. In addition, the higher T-c as well as the lower Nd substitution can be achieved when using the lower growth temperature. These results are consistently interpreted by the NdO1.5-BaO-CuO ternary phase diagram. (C) 1998 Elsevier Science B.V.
What problem does this paper attempt to address?