Abstract:IMD MgB2 long wire is produced by alternating use of rotary‐swaging and drawing strategy. A 600 m 30‐filament MgB2 wire is obtained here with the Je and Jc reaches to 8.0 × 104 A cm−2 and 7.6 × 105 A cm−2 (at 4.2 K, 4 T), respectively. The MgB2 coil made by the wire obtains a center field of 5.71 T. The poor deformation ability of magnesium rods makes it challenging to fabricate long MgB2 inner magnesium diffusion (IMD) wires, further seriously limiting the application of high‐performance MgB2 wires. A 600 m IMD 30‐filament MgB2 wire is fabricate by alternating use of rotary‐swaging and drawing strategy. The critical current density (Jc) and the critical engineering current density (Je) are 8.0 × 104 A cm−2 and 7.6 × 105 A cm−2 (at 4.2 K, 4 T), respectively, which are some of the best performances reported so far. The flux‐pinning behavior of the MgB2 wires is investigated, and the surface pinning behavior is found to be dominant in the IMD 30‐filament wire in the whole field range at 4.2 K. The critical point for the IMD 30‐filament MgB2 wire to keep high performance in high fields is revealed by comparing it with the reference wires. Then, 520 m of wire are cut from the 30‐filament MgB2 wire and wound into a coil. The center field of the coil is 5.71 T at 4.2 K when the current loads to 219 A, which is the highest value among the IMD MgB2 coils. This work made breakthroughs in the wire length, filament numbers, and transport performance of IMD MgB2 wire, while also providing a paradigm study for exploring the in situ magnetic performance of multi‐filament wires.

The Critical Current Density of Advanced Internal-Mg-diffusion-processed MgB2wires

High transport critical currents in dense, metal-clad superconductor wires of MgB2

Transport Behavior and Critical Current Densities in MgB2 Wires

Improving Superconducting Properties of 100 M Class MgB2 Wire with 18+1 Filaments Produced Via Internal Mg Diffusion Process

High transport critical current density obtained for Powder-In-Tube-processed MgB2 tapes and wires using stainless steel and Cu-Ni tubes

Improving superconducting properties of 100 m class MgB 2 wire with 18+1 filaments produced via internal Mg diffusion process

Fabrication and Properties of Multifilamentary MgB2 Wires by In-Situ Powder-in-tube Process

Microstructure and high critical current of powder in tube MgB2

Enhancement of Critical Current Density in Graphite Doped Mgb2 Wires

Development of Ti-sheathed MgB<sub>2</sub> wires with high critical current density

High transport critical current in MgB2/Fe wire by in situ powder-in-tube process

Fabrication of MgB2 Coil with the Center Field of 5.71 Tesla Using 520‐m Inner Magnesium Diffusion Wire

Critical Current Densities and N-Values of Mgb2 Strands over A Wide Range of Temperatures and Fields

Superconducting Properties and Microstructure in MgB 2 Bulks, Wires and Tapes

Influence of the Preparation Process on Microstructure, Critical Current Density and Tc of MgB2 Powder-In-Tube Wires

Influence of Heat-Treatment and Element Doping on Critical Current Density of MgB_2/Fe/Cu Wires Fabricated by in-Situ PIT Technique

Very Large Engineering Critical Current Density Properties in a (6+1)-Structure MgB2 Superconducting Cable at 20 K

Influence of heat-treatment and element doping on critical current density of MgB2/Fe/Cu wires fabricated by in-situ PIT technique

Supercurrents in magnesium diboride/metal composite wire

Enhancement of Critical Current Density by a “Mgb2-Mgb4” Reversible Reaction in Self-Sintered Ex-Situ MgB2 Bulks

Effects of Mgo Impurities and Micro-Cracks on the Critical Current Density of Ti-Sheathed Mgb2 Wires