Abstract:Understanding the initiating and suppression mechanisms of existing defects are the key to optimizing the ultra-precision grinding process of hard and brittle materials. This paper discusses the effects of grinding damage on material removal mechanism from the perspectives of residual scratch depth, scratch morphology and normal scratching force, through conducting the contrast variable-depth nano-scratch experiment on polished and ground monocrystalline silicon and establishing the single grain scratching Smoothed Particle Hydrodynamics (SPH) model. The experimental and simulation results show that radial crack on ground silicon surface is almost invisible due to the existence of grinding marks, which indicates that it is difficult to judge the ductile brittle transition (DBT) point by the traditional method of observing cracks. With the increase of penetration depth, pop-in will occur in the residual scratch depth of polished and ground silicon, indicating that the material removal mode has transformed, which provides an important basis for judging the DBT point. The DBT critical normal scratching force (38.93 mN) and residual scratch depth (−0.14 μm) of ground silicon are much higher than those of polished silicon, implying ground silicon is easier to achieve ductile processing. Meanwhile, when the penetration depth is the same, compared to polished silicon, the normal scratching force of ground silicon is generally larger. Finally, a single grain scratching SPH model of pre-stressed silicon is established. And the simulated phenomenon and conclusions are consistent with the experiment, which proves that the surface compressive stress is an important factor that causes the removal characteristics of ground silicon to be different from polished silicon. This study provides a theoretical basis for understanding the ultra-precision grinding removal mechanism of hard and brittle materials.

Relationship Between Grinding Process and the Parameters of Subsurface Damage Based on the Image Processing

The Influence of Grinding Process Parameters on Transmittance and Absorbance of the Optical Components

The Influence of Subsurface Damage’s Micro Crack on the Optical Properties of the Optical Components

Experimental Research on the Effect of Grinding Parameters on Ceramic Machined Surface Roughness

Experimental investigation on grinding-induced surface damage of Fiber Reinforced Ceramic Matrix Composites

Prediction and Verification Analysis of Grinding Force in the Single Grain Grinding Process of Fused Silica Glass

Analysis on Ground Surface Damage of Quartz Fiber-Reinforced Quartz Composites

Method of Damage Characterization of Engineering Ceramics Grinding Surface

Effect of Grinding Parameters on Surface Roughness and Subsurface Damage and Their Evaluation in Fused Silica.

Numerical Investigation of the Evolution of Grit Fracture and Its Impact on Cutting Performance in Single Grit Grinding

Relationship Between Surface Roughness and Subsurface Crack Depth During Grinding of Optical Glass BK7

Optimization of grinding process for hard and brittle materials based on damage evolution mechanism

Characterization Methods of Subsurface Cracks in Grinding of Optical Elements

Prediction of Grinding Induced Subsurface Damage of Optical Materials

Subsurface Damage in Sapphire Ultra-Precision Grinding

Theoretical Model and Digital Extraction of Subsurface Damage in Ground Fused Silica

Analytical Modelling of Both Parallel and Cross Grinding with Arc-Shaped Wheel for Grinding-Induced Damage and Grinding Force

Models of grinding-induced surface and subsurface damages in fused silica considering strain rate and micro shape/geometry of abrasive

Relationship Between Subsurface Damage and Surface Roughness of Glass BK7 in Rotary Ultrasonic Machining and Conventional Grinding Processes

Interference mechanism and damage accumulation in high-speed cross scratches on hard brittle materials

Effect of grinding damage on cutting force and ductile machining during single grain scratching of monocrystalline silicon